Material Notes:
Glass fiber-reinforced polyester molding compound. Very good mechanical strength, very good electrical properties and dimensional stability, heat resistant up to 500°C for short time - usable for solder baths, excellent processability with very short cycle times, low mould wear. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS). Processing: Injection or Transfer. Applications: Connectors, Bobbins, Housings and Mounting platesInformation provided by the Raschig Group
Physical Properties Metric English Comments
Specific Gravity 2.00 - 2.20 g/cc
2.00 - 2.20 g/cc
ISO 1183
Apparent Bulk Density 0.800 - 0.950 g/cc
0.0289 - 0.0343 lb/in³
ISO 60
Water Absorption <= 0.30 %

@Temperature 23.0 °C,
Time 86400 sec
<= 0.30 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.0025 - 0.0045 cm/cm
0.0025 - 0.0045 in/in
Injection and Compression; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength, Yield 35.0 - 60.0 MPa
5080 - 8700 psi
Compression; ISO 527
60.0 - 70.0 MPa
8700 - 10200 psi
Injection; ISO 527
Modulus of Elasticity 6.00 - 9.00 GPa
870 - 1310 ksi
Compression; ISO 527
13.0 - 15.0 GPa
1890 - 2180 ksi
Injection; ISO 527
Flexural Strength 80.0 - 100 MPa
11600 - 14500 psi
Compression; ISO 178
140 - 160 MPa
20300 - 23200 psi
Injection; ISO 178
Flexural Modulus 8.00 - 12.0 GPa
1160 - 1740 ksi
Compression; ISO 178
16.0 - 18.0 GPa
2320 - 2610 ksi
Injection; ISO 178
Compressive Strength 120 - 170 MPa
17400 - 24700 psi
Injection; ISO 604
Charpy Impact Unnotched 0.500 - 1.00 J/cm²

@Temperature 23.0 °C
2.38 - 4.76 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179/ 1eU
1.50 - 1.80 J/cm²

@Temperature 23.0 °C
7.14 - 8.57 ft-lb/in²

@Temperature 73.4 °F
Injection; ISO 179/ 1eU
Charpy Impact, Notched 0.400 - 0.500 J/cm²

@Temperature 23.0 °C
1.90 - 2.38 ft-lb/in²

@Temperature 73.4 °F
Compression; ISO 179/ 1eA
0.500 - 0.600 J/cm²

@Temperature 23.0 °C
2.38 - 2.86 ft-lb/in²

@Temperature 73.4 °F
Injection; ISO 179/ 1eA
Thermal Properties Metric English Comments
CTE, linear 10.0 - 20.0 µm/m-°C

@Temperature 50.0 - 100 °C
5.56 - 11.1 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Thermal Conductivity 0.900 - 1.10 W/m-K
6.25 - 7.63 BTU-in/hr-ft²-°F
ASTM E1461
Deflection Temperature at 1.8 MPa (264 psi) >= 200 °C
>= 392 °F
ISO 75-A
Deflection Temperature at 8.0 MPa 110 - 130 °C
230 - 266 °F
ISO 75-C
Flammability, UL94 V-0

@Thickness 1.40 mm
V-0

@Thickness 0.0551 in
Shrinkage <= 0.050 %

@Temperature 110 °C,
Time 605000 sec
<= 0.050 %

@Temperature 230 °F,
Time 168 hour
Post shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 - 1.00e+15 ohm-cm
1.00e+14 - 1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 - 1.00e+14 ohm
1.00e+13 - 1.00e+14 ohm
IEC 60093
Dielectric Constant 4.0 - 5.0

@Frequency 1.00e+6 Hz
4.0 - 5.0

@Frequency 1.00e+6 Hz
IEC 60250
5.0 - 6.0

@Frequency 100 Hz
5.0 - 6.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 25.0 - 35.0 kV/mm
635 - 889 kV/in
IEC 60243-1
Dissipation Factor 0.010 - 0.030

@Frequency 100 Hz
0.010 - 0.030

@Frequency 100 Hz
IEC 60250
0.010 - 0.030

@Frequency 1.00e+6 Hz
0.010 - 0.030

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
CTI; IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature 15.0 - 25.0 °C
6.00 Month

@Temperature 59.0 - 77.0 °F
Descriptive Properties Value Comments
Arc Resistance 4 Stufe
ASTM D495
Glow wire flammability test 960/1
IEC 60695 2-12
Glow wire ignitability test 930/1
IEC 60695 2-13
Water Absorption < 20 mg
ISO 62; 24h / 23°C