Raschig Group 3572 Epoxy

Category Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler , Filled/Reinforced Thermoset
Manufacturer Raschig Group
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group 3572 Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass-fiber reinforced epoxy molding compound. Good mechanical strength and electrical strength, enhanced elasticity for ensuring good sealing under extreme heat and/or humidity, good chemical resistance, exceptional metal adhesion, very good flame retardance. Suitable for pelleting and preheating. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS).Processing: Transfer molding Primary application: Embedding metal parts for metallurgical tests.Information provided by the Raschig Group
Physical Properties Metric English Comments
Specific Gravity 2.10 - 2.20 g/cc
2.10 - 2.20 g/cc
ISO 1183
Apparent Bulk Density 1.00 - 1.15 g/cc
0.0361 - 0.0415 lb/in³
ISO 60
Water Absorption <= 0.100 %

@Temperature 23.0 °C,
Time 86400 sec
<= 0.100 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.0025 - 0.0045 cm/cm
0.0025 - 0.0045 in/in
(longitudinal); ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength 50.0 - 70.0 MPa
7250 - 10200 psi
ISO 527
Flexural Strength 100 - 120 MPa
14500 - 17400 psi
ISO 178
Flexural Modulus 11.0 - 13.0 GPa
1600 - 1890 ksi
ISO 178
Compressive Strength 150 - 200 MPa
21800 - 29000 psi
ISO 604
Charpy Impact Unnotched 4.00 - 6.00 J/cm²

@Temperature 23.0 °C
19.0 - 28.6 ft-lb/in²

@Temperature 73.4 °F
ISO 179/ 1eU
Charpy Impact, Notched 0.200 - 0.300 J/cm²
0.952 - 1.43 ft-lb/in²
ISO 179/1EA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 - 40.0 µm/m-°C

@Temperature 50.0 - 150 °C
5.56 - 22.2 µin/in-°F

@Temperature 122 - 302 °F
Post shrinkage; ISO 11359-2
Thermal Conductivity 0.500 - 0.700 W/m-K
3.47 - 4.86 BTU-in/hr-ft²-°F
ASTM E1461
Deflection Temperature at 1.8 MPa (264 psi) 110 - 130 °C
230 - 266 °F
ISO 75-A
Deflection Temperature at 8.0 MPa 100 - 120 °C
212 - 248 °F
ISO 75-C
Flammability, UL94 V-0

@Thickness 0.700 mm
V-0

@Thickness 0.0276 in
Shrinkage <= 0.0500 %

@Temperature 110 °C,
Time 605000 sec
<= 0.0500 %

@Temperature 230 °F,
Time 168 hour
Post Shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 - 1.00e+15 ohm-cm
1.00e+14 - 1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+13 - 1.00e+14 ohm
1.00e+13 - 1.00e+14 ohm
IEC 60093
Dielectric Constant 4.0 - 6.0

@Frequency 100 Hz
4.0 - 6.0

@Frequency 100 Hz
IEC 60250
4.0 - 6.0

@Frequency 1.00e+6 Hz
4.0 - 6.0

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 15.0 - 20.0 kV/mm
381 - 508 kV/in
IEC 60243-1
Dissipation Factor 0.010 - 0.020

@Frequency 1.00e+6 Hz
0.010 - 0.020

@Frequency 1.00e+6 Hz
IEC 60250
0.020 - 0.030

@Frequency 100 Hz
0.020 - 0.030

@Frequency 100 Hz
IEC 60250
Comparative Tracking Index >= 325 V
>= 325 V
CTI; IEC 60112
Processing Properties Metric English Comments
Mold Temperature 170 - 190 °C
338 - 374 °F
Shelf Life 6.00 Month

@Temperature 15.0 - 25.0 °C
6.00 Month

@Temperature 59.0 - 77.0 °F
Descriptive Properties Value Comments
Arc Resistance 4 Stufe
ASTM D495
Glow wire flammability test 900/1
IEC 60695 2-12
Glow wire ignitability test 900/1
IEC 60695 2-13
Water Absorption <10 mg
ISO 62; 24h / 23°C