Raschig Group DECAL® 1760 Phenolic

Category Polymer , Thermoset , Phenolic
Manufacturer Raschig Group
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group DECAL® 1760 Phenolic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass-fiber reinforced phenolic molding compound. Very good electrical properties, good chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS)Processing: Injection and Compression moldingInformation provided by Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.60 - 1.75 g/cc
1.60 - 1.75 g/cc
ISO 1183
Apparent Bulk Density 0.600 - 0.800 g/cc
0.0217 - 0.0289 lb/in³
ISO 60
Water Absorption <= 0.500 %

@Temperature 23.0 °C,
Time 86400 sec
<= 0.500 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.00600 - 0.00800 cm/cm
0.00600 - 0.00800 in/in
Injection; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength 50.0 - 70.0 MPa
7250 - 10200 psi
Injection; ISO 527
Modulus of Elasticity 5.00 - 7.00 GPa
725 - 1020 ksi
Injection; ISO 527
Flexural Strength 100 - 120 MPa
14500 - 17400 psi
Injection; ISO 178
Flexural Modulus 7.00 - 9.00 GPa
1020 - 1310 ksi
Injection; ISO 178
Compressive Strength 150 - 200 MPa
21800 - 29000 psi
ISO 604
Charpy Impact Unnotched 0.600 - 0.900 J/cm²
2.86 - 4.28 ft-lb/in²
Injection; ISO 179/1eU
Charpy Impact, Notched 0.200 - 0.400 J/cm²
0.952 - 1.90 ft-lb/in²
Injection; ISO 179/1eA
Thermal Properties Metric English Comments
Thermal Conductivity 0.400 - 0.600 W/m-K
2.78 - 4.16 BTU-in/hr-ft²-°F
ASTM E1461
Deflection Temperature at 1.8 MPa (264 psi) >= 200 °C
>= 392 °F
ISO 75-A
Deflection Temperature at 8.0 MPa 160 - 180 °C
320 - 356 °F
ISO 75-C
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Shrinkage 0.100 - 0.200 %

@Temperature 110 °C,
Time 605000 sec
0.100 - 0.200 %

@Temperature 230 °F,
Time 168 hour
Post shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 - 1.00e+13 ohm-cm
1.00e+12 - 1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 - 1.00e+11 ohm
1.00e+10 - 1.00e+11 ohm
IEC 60093
Dielectric Constant 4.00 - 6.00

@Frequency 1.00e+6 Hz
4.00 - 6.00

@Frequency 1.00e+6 Hz
IEC 60250
10.0 - 12.0

@Frequency 100 Hz
10.0 - 12.0

@Frequency 100 Hz
IEC 60250
Dielectric Strength 20.0 - 30.0 kV/mm
508 - 762 kV/in
IEC 60243-1
Dissipation Factor 0.0400 - 0.0600

@Frequency 1.00e+6 Hz
0.0400 - 0.0600

@Frequency 1.00e+6 Hz
IEC 60250
0.600 - 0.800

@Frequency 100 Hz
0.600 - 0.800

@Frequency 100 Hz
IEC 60250
Arc Resistance 120 - 180 sec
120 - 180 sec
ASTM D495
Comparative Tracking Index >= 275 V
>= 275 V
IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature 20.0 - 30.0 °C
6.00 Month

@Temperature 68.0 - 86.0 °F
Descriptive Properties Value Comments
Glow wire flammability test 960/1
IEC 60695 2-12
Glow wire ignitability test 960/1
IEC 60695 2-13
Water Absorption <40 mg
24 hr, 23°C; ISO 62