Raschig Group DECAL® 666/8/2B Phenolic

Category Polymer , Thermoset , Phenolic
Manufacturer Raschig Group
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group DECAL® 666/8/2B Phenolic.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS)Processing: Injection and compression molding Applications: CommutatorsInformation provided by Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.80 - 1.90 g/cc
1.80 - 1.90 g/cc
ISO 1183
Apparent Bulk Density 0.800 - 1.00 g/cc
0.0289 - 0.0361 lb/in³
ISO 60
Water Absorption <= 0.200 %

@Temperature 23.0 °C,
Time 86400 sec
<= 0.200 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.00200 - 0.00400 cm/cm
0.00200 - 0.00400 in/in
Injection and Compression; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength 60.0 - 90.0 MPa
8700 - 13100 psi
Compression; ISO 527
70.0 - 90.0 MPa
10200 - 13100 psi
Injection; ISO 527
Modulus of Elasticity 6.00 - 8.00 GPa
870 - 1160 ksi
Compression; ISO 527
7.00 - 9.00 GPa
1020 - 1310 ksi
Injection; ISO 527
Flexural Strength 100 - 120 MPa
14500 - 17400 psi
Compression; ISO 178
140 - 160 MPa
20300 - 23200 psi
Injection; ISO 178
Flexural Modulus 13.0 - 17.0 GPa
1890 - 2470 ksi
Compression; ISO 178
14.0 - 18.0 GPa
2030 - 2610 ksi
Injection; ISO 178
Compressive Strength 200 - 250 MPa
29000 - 36300 psi
ISO 604
Charpy Impact Unnotched 0.500 - 0.700 J/cm²
2.38 - 3.33 ft-lb/in²
Compression; ISO 179/1eU
0.700 - 0.900 J/cm²
3.33 - 4.28 ft-lb/in²
Injection; ISO 179/1eU
Charpy Impact, Notched 0.200 - 0.400 J/cm²
0.952 - 1.90 ft-lb/in²
Injection and Compression; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 10.0 - 15.0 µm/m-°C

@Temperature 50.0 - 150 °C
5.56 - 8.33 µin/in-°F

@Temperature 122 - 302 °F
ISO 11359-2
Thermal Conductivity 0.400 - 0.600 W/m-K
2.78 - 4.16 BTU-in/hr-ft²-°F
ASTM E1461
Deflection Temperature at 1.8 MPa (264 psi) >= 180 °C
>= 356 °F
ISO 75-A
Deflection Temperature at 8.0 MPa 140 - 160 °C
284 - 320 °F
ISO 75-C
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Shrinkage <= 0.0500 %

@Temperature 110 °C,
Time 605000 sec
<= 0.0500 %

@Temperature 230 °F,
Time 168 hour
Post shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 - 1.00e+13 ohm-cm
1.00e+12 - 1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 - 1.00e+11 ohm
1.00e+10 - 1.00e+11 ohm
IEC 60093
Dielectric Constant 4.00 - 6.00

@Frequency 1.00e+6 Hz
4.00 - 6.00

@Frequency 1.00e+6 Hz
IEC 60250
6.00 - 8.00

@Frequency 100 Hz
6.00 - 8.00

@Frequency 100 Hz
IEC 60250
Dielectric Strength 20.0 - 30.0 kV/mm
508 - 762 kV/in
IEC 60243-1
Dissipation Factor 0.00500 - 0.0100

@Frequency 100 Hz
0.00500 - 0.0100

@Frequency 100 Hz
IEC 60250
0.0200 - 0.0300

@Frequency 1.00e+6 Hz
0.0200 - 0.0300

@Frequency 1.00e+6 Hz
IEC 60250
Arc Resistance 180 - 240 sec
180 - 240 sec
ASTM D495
Comparative Tracking Index >= 200 V
>= 200 V
IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature 20.0 - 30.0 °C
6.00 Month

@Temperature 68.0 - 86.0 °F
Descriptive Properties Value Comments
Glow wire flammability test 960/1
IEC 60695 2-12
Glow wire ignitability test 960/1
IEC 60695 2-13
Water Absorption <20 mg
24 hr, 23°C; ISO 62