Raschig Group RALUPOL® 2100 UP Polyester

Category Polymer , Thermoset , Polyester, TS
Manufacturer Raschig Group
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group RALUPOL® 2100 UP Polyester.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS).Processing: Injection and compression molding Primary application: Safety cut outs, Contactors, SwitchesInformation provided by Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.65 - 1.85 g/cc
1.65 - 1.85 g/cc
ISO 1183
Apparent Bulk Density 0.750 - 1.00 g/cc
0.0271 - 0.0361 lb/in³
ISO 60
Water Absorption <= 1.20 %

@Temperature 23.0 °C,
Time 86400 sec
<= 1.20 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage, Flow 0.00700 - 0.0100 cm/cm
0.00700 - 0.0100 in/in
Injection; ISO 2577
0.00800 - 0.0110 cm/cm
0.00800 - 0.0110 in/in
Compression; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength 25.0 - 40.0 MPa
3630 - 5800 psi
Compression; ISO 527
40.0 - 50.0 MPa
5800 - 7250 psi
Injection; ISO 527
Modulus of Elasticity 4.00 - 6.00 GPa
580 - 870 ksi
Compression; ISO 527
5.00 - 8.00 GPa
725 - 1160 ksi
Injection; ISO 527
Flexural Strength 50.0 - 80.0 MPa
7250 - 11600 psi
Compression; ISO 178
80.0 - 120 MPa
11600 - 17400 psi
Injection; ISO 178
Flexural Modulus 6.00 - 9.00 GPa
870 - 1310 ksi
Compression; ISO 178
7.00 - 10.0 GPa
1020 - 1450 ksi
Injection; ISO 178
Compressive Strength 150 - 200 MPa
21800 - 29000 psi
ISO 604
Charpy Impact Unnotched 0.500 - 0.800 J/cm²
2.38 - 3.81 ft-lb/in²
Compression; ISO 179/1eU
0.600 - 1.00 J/cm²
2.86 - 4.76 ft-lb/in²
Injection; ISO 179/1eU
Charpy Impact, Notched 0.100 - 0.200 J/cm²
0.476 - 0.952 ft-lb/in²
Compression; ISO 179/1eA
0.150 - 0.250 J/cm²
0.714 - 1.19 ft-lb/in²
Injection; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 24.0 - 45.0 µm/m-°C

@Temperature 50.0 - 100 °C
13.3 - 25.0 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Thermal Conductivity 0.900 - 1.00 W/m-K
6.25 - 6.94 BTU-in/hr-ft²-°F
ASTM E1461
Maximum Service Temperature, Air 13.0 °C

@Time 7.20e+7 sec
55.4 °F

@Time 20000 hour
IEC 60216/T1
190 °C

@Time <=180000 sec
374 °F

@Time <=50.0 hour
IEC 60216/T1
Deflection Temperature at 1.8 MPa (264 psi) >= 180 °C
>= 356 °F
ISO 75-A
Deflection Temperature at 8.0 MPa 80.0 - 120 °C
176 - 248 °F
ISO 75-C
Flammability, UL94 V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Shrinkage 0.200 - 0.400 %

@Temperature 110 °C,
Time 605000 sec
0.200 - 0.400 %

@Temperature 230 °F,
Time 168 hour
Post shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 - 1.00e+13 ohm-cm
1.00e+12 - 1.00e+13 ohm-cm
IEC 60093
Surface Resistance 1.00e+11 - 1.00e+12 ohm
1.00e+11 - 1.00e+12 ohm
IEC 60093
Dielectric Constant 4.00 - 6.00

@Frequency 1.00e+6 Hz
4.00 - 6.00

@Frequency 1.00e+6 Hz
IEC 60250
5.00 - 7.00

@Frequency 100 Hz
5.00 - 7.00

@Frequency 100 Hz
IEC 60250
Dielectric Strength 20.0 - 30.0 kV/mm
508 - 762 kV/in
IEC 60243-1
Dissipation Factor 0.0300 - 0.0500

@Frequency 1.00e+6 Hz
0.0300 - 0.0500

@Frequency 1.00e+6 Hz
IEC 60250
0.600 - 0.800

@Frequency 100 Hz
0.600 - 0.800

@Frequency 100 Hz
IEC 60250
Arc Resistance 180 - 240 sec
180 - 240 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature 15.0 - 25.0 °C
6.00 Month

@Temperature 59.0 - 77.0 °F
Descriptive Properties Value Comments
Glow wire flammability test 960/1
IEC 60695 2-12
Glow wire ignitability test 850/1
IEC 60695 2-13
Water Absorption <75 mg
24 hr, 23°C; ISO 62