Raschig Group RALUPOL® 2200 UP Polyester

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS
Manufacturer Raschig Group
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group RALUPOL® 2200 UP Polyester.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Organically filled polyester molding compound. Low post-shrinkage, good electrical values and mechanical properties, high surface quality and good color stability (non-yellowing). This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS).Processing: Injection molding Primary application: Oven fittingsInformation provided by the Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.70 - 1.90 g/cc
1.70 - 1.90 g/cc
ISO 1183
Apparent Bulk Density 0.750 - 1.00 g/cc
0.0271 - 0.0361 lb/in³
ISO 60
Water Absorption <= 2.0 %

@Temperature 23.0 °C,
Time 86400 sec
<= 2.0 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
Injection; ISO 2257
Mechanical Properties Metric English Comments
Tensile Strength 50.0 - 70.0 MPa
7250 - 10200 psi
ISO 527
Modulus of Elasticity 5.00 - 8.00 GPa
725 - 1160 ksi
ISO 527
Flexural Strength 90.0 - 120 MPa
13100 - 17400 psi
Injection; ISO 178
Flexural Modulus 8.00 - 10.0 GPa
1160 - 1450 ksi
Injection; ISO 178
Compressive Strength 150 - 200 MPa
21800 - 29000 psi
ISO 604
Charpy Impact Unnotched 0.700 - 1.20 J/cm²

@Temperature 23.0 °C
3.33 - 5.71 ft-lb/in²

@Temperature 73.4 °F
Injection; ISO 179/ 1eU
Charpy Impact, Notched 0.200 - 0.300 J/cm²

@Temperature 23.0 °C
0.952 - 1.43 ft-lb/in²

@Temperature 73.4 °F
Injection; ISO 179/ 1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 15.0 - 25.0 µm/m-°C

@Temperature 50.0 - 100 °C
8.33 - 13.9 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Thermal Conductivity 0.500 - 0.600 W/m-K
3.47 - 4.16 BTU-in/hr-ft²-°F
ASTM E1461
Maximum Service Temperature, Air 130 °C
266 °F
20,000 h; IEC 216/T1
190 °C
374 °F
< 50 h; IEC 216/T1
Deflection Temperature at 1.8 MPa (264 psi) >= 110 °C
>= 230 °F
ISO 75-A
Deflection Temperature at 8.0 MPa 70.0 - 120 °C
158 - 248 °F
Injection; ISO 75-C
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Shrinkage 0.10 - 0.40 %

@Temperature 110 °C,
Time 605000 sec
0.10 - 0.40 %

@Temperature 230 °F,
Time 168 hour
Post shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+11 - 1.00e+12 ohm-cm
1.00e+11 - 1.00e+12 ohm-cm
IEC 60093
Surface Resistance 1.00e+10 - 1.00e+11 ohm
1.00e+10 - 1.00e+11 ohm
IEC 60093
Dielectric Strength 20.0 - 30.0 kV/mm
508 - 762 kV/in
IEC 60250
Comparative Tracking Index 600 V
600 V
PTI; IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature 15.0 - 25.0 °C
6.00 Month

@Temperature 59.0 - 77.0 °F
Descriptive Properties Value Comments
Arc Resistance 4 Stufe
ASTM D495
Water Absorption <130 MG
ISO 62; 24h / 23°C