Raschig Group RALUPOL® 8602 UP

Category Polymer , Thermoset , Filled/Reinforced Thermoset , Polyester, TS
Manufacturer Raschig Group
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Raschig Group RALUPOL® 8602 UP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Glass-fiber reinforced polyester molding compound. Mold shrinkage similar to phenolic molding compounds, low post-shrinkage, good electrical values, excellent heat resistance, good mechanical strength, excellent surface quality and excellent color stability (non-yellowing), low wear. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (WEEE) and 2006/122 (PFOS).Processing: Injection molding Primary application: Oven fittingsInformation provided by the Raschig Group
Physical Properties Metric English Comments
Specific Gravity 1.90 - 2.10 g/cc
1.90 - 2.10 g/cc
ISO 1183
Apparent Bulk Density 0.750 - 1.00 g/cc
0.0271 - 0.0361 lb/in³
ISO 60
Water Absorption <= 0.55 %

@Temperature 23.0 °C,
Time 86400 sec
<= 0.55 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Linear Mold Shrinkage 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
Injection; ISO 2257
Mechanical Properties Metric English Comments
Tensile Strength, Yield 40.0 - 70.0 MPa
5800 - 10200 psi
Injection; ISO 527
Modulus of Elasticity 10.0 - 12.0 GPa
1450 - 1740 ksi
Injection; ISO 527
Flexural Strength 90.0 - 120 MPa
13100 - 17400 psi
Injection; ISO 178
Flexural Modulus 14.0 - 16.0 GPa
2030 - 2320 ksi
Injection; ISO 178
Compressive Strength 150 - 200 MPa
21800 - 29000 psi
ISO 604
Charpy Impact Unnotched 0.500 - 1.00 J/cm²

@Temperature 23.0 °C
2.38 - 4.76 ft-lb/in²

@Temperature 73.4 °F
Injection; ISO 179/ 1eU
Charpy Impact, Notched 0.200 - 0.400 J/cm²

@Temperature 23.0 °C
0.952 - 1.90 ft-lb/in²

@Temperature 73.4 °F
Injection; ISO 179/ 1eA
Thermal Properties Metric English Comments
CTE, linear 10.0 - 20.0 µm/m-°C

@Temperature 50.0 - 100 °C
5.56 - 11.1 µin/in-°F

@Temperature 122 - 212 °F
ISO 11359-2
Thermal Conductivity 0.500 - 0.600 W/m-K
3.47 - 4.16 BTU-in/hr-ft²-°F
ASTM E1461
Maximum Service Temperature, Air 150 °C
302 °F
20,000 h; IEC 216/T1
200 °C
392 °F
< 50 h; IEC 216/T1
Deflection Temperature at 1.8 MPa (264 psi) 140 - 170 °C
284 - 338 °F
Injection; ISO 75-A
Deflection Temperature at 8.0 MPa 70.0 - 130 °C
158 - 266 °F
Injection; ISO 75-C
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Shrinkage <= 0.10 %

@Temperature 110 °C,
Time 605000 sec
<= 0.10 %

@Temperature 230 °F,
Time 168 hour
Post shrinkage; ISO 2577
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 - 1.00e+14 ohm-cm
1.00e+13 - 1.00e+14 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 - 1.00e+13 ohm
1.00e+12 - 1.00e+13 ohm
IEC 60093
Comparative Tracking Index 600 V
600 V
PTI; IEC 60112
Processing Properties Metric English Comments
Shelf Life 6.00 Month

@Temperature 15.0 - 25.0 °C
6.00 Month

@Temperature 59.0 - 77.0 °F
Descriptive Properties Value Comments
Arc Resistance 4 Stufe
ASTM D495
Water Absorption <40 mg
ISO 62; 24h / 23°C