Ravago Manufacturing Americas Hylac® GP74G20 ABS, 20% Glass Fiber Reinforced

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Glass Fiber Filled
Manufacturer Ravago Manufacturing Americas, LLC
Trade Name Hylac®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ravago Manufacturing Americas Hylac® GP74G20 ABS, 20% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Ravago.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm
0.0010 - 0.0040 in/in
ASTM D955
Melt Flow 2.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
2.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 75.8 MPa
11000 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ASTM D638
Flexural Yield Strength 103 MPa
15000 psi
ASTM D790
Flexural Modulus 5.17 GPa
750 ksi
ASTM D790
Izod Impact, Notched 0.587 J/cm
1.10 ft-lb/in
73°F, 0.125 in; ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 97.8 °C
208 °F
Unannealed; ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 191 - 199 °C
375 - 390 °F
Middle Barrel Temperature 204 - 221 °C
400 - 430 °F
Front Barrel Temperature 210 - 224 °C
410 - 435 °F
Nozzle Temperature 210 - 229 °C
410 - 445 °F
Melt Temperature 241 °C
465 °F
Mold Temperature 48.9 - 60.0 °C
120 - 140 °F
Moisture Content <= 0.10 %
<= 0.10 %
Injection Pressure 7.24 - 8.27 MPa
1050 - 1200 psi
Back Pressure 0.483 - 0.827 MPa
70.0 - 120 psi
Shot Size 40 - 80 %
40 - 80 %
Screw Speed 50 - 70 rpm
50 - 70 rpm
Descriptive Properties Value Comments
Holding Pressure 900 to 1000 psi
Injection Rate Slow-Moderate