Ravago Manufacturing Americas Hylex® P1325L Polycarbonate, UV Stabilized, High Flow, Mold Release

Category	Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Molded
Manufacturer	Ravago Manufacturing Americas, LLC
Trade Name	Hylex®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ravago Manufacturing Americas Hylex® P1325L Polycarbonate, UV Stabilized, High Flow, Mold Release.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Entec's proprietary products include a full range of compounds in the Nylon 6/6, Nylon 6, ABS, PBT, Polycarbonate, PC/ABS, PC/ASA, PC/PBT, and PPO/PPE resin families.Information provided by Entec.

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/in³	ASTM D792
Water Absorption	0.15 %	0.15 %	24 hrs; ASTM D570
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	ASTM D955
Melt Flow	25 g/10 min @Load 1.20 kg, Temperature 300 °C	25 g/10 min @Load 2.65 lb, Temperature 572 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	80	80	ASTM D785
Tensile Strength at Break	68.9 MPa	10000 psi	ASTM D638
Elongation at Break	115 %	115 %	ASTM D638
Flexural Strength	91.0 MPa	13200 psi	ASTM D790
Flexural Modulus	2.31 GPa	335 ksi	ASTM D790
Izod Impact, Notched	6.41 J/cm	12.0 ft-lb/in	73°F, 0.125 in; ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	132 °C	270 °F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	127 °C	260 °F	Unannealed; ASTM D648
Vicat Softening Point	154 °C	310 °F	ASTM D1525
Flammability, UL94	V-2 @Thickness 1.50 mm	V-2 @Thickness 0.0591 in
	V-2 @Thickness 3.00 mm	V-2 @Thickness 0.118 in
	V-0 @Thickness 6.00 mm	V-0 @Thickness 0.236 in

Optical Properties	Metric	English	Comments
Refractive Index	1.585	1.585	ASTM D542
Haze	0.50 - 0.80 %	0.50 - 0.80 %	125 mil; ASTM D1003
Transmission, Visible	89 - 91 %	89 - 91 %	125 mil; ASTM D1003

Electrical Properties	Metric	English	Comments
Volume Resistivity	4.00e+16 ohm-cm	4.00e+16 ohm-cm	ASTM D257
Dielectric Strength	16.1 kV/mm	410 kV/in	in Air, 0.125 in; ASTM D149
Arc Resistance	120 sec	120 sec	ASTM D495

Processing Properties	Metric	English
Rear Barrel Temperature	232 - 254 °C	450 - 490 °F
Middle Barrel Temperature	243 - 266 °C	470 - 510 °F
Front Barrel Temperature	260 - 271 °C	500 - 520 °F
Nozzle Temperature	260 - 271 °C	500 - 520 °F
Melt Temperature	266 - 277 °C	510 - 530 °F
Mold Temperature	65.6 - 87.8 °C	150 - 190 °F
Drying Temperature	121 °C	250 °F
Dry Time	3 - 12 hour	3 - 12 hour
Moisture Content	<= 0.020 %	<= 0.020 %
Injection Pressure	5.52 - 12.4 MPa	800 - 1800 psi
Back Pressure	0.483 - 1.03 MPa	70.0 - 150 psi
Shot Size	40 - 60 %	40 - 60 %
Screw Speed	40 - 70 rpm	40 - 70 rpm

Descriptive Properties	Value	Comments
Holding Pressure	500 to 1000 psi