Renegade Materials Corporation RM-5001 Cyanate Ester Prepreg, 3K 8HS Fabric

Category Polymer , Thermoset , Filled/Reinforced Thermoset
Manufacturer Renegade Materials Corporation
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Renegade Materials Corporation RM-5001 Cyanate Ester Prepreg, 3K 8HS Fabric.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
RM-5001 cyanate ester is a very low outgassing, toughened, high performance prepreg. Straightforward 350°F Cure Designed for the unique requirements of satellite and missile structuresLow shrinkage during cureDeveloped for consistent handling and superior performance Continuous service up to and including 350F with post cureAvailable in woven and unidirectional product forms using all fibers including carbon, quartz and S2 glass Nano-enhancement for tailored laminate properties and multi-functional performanceLow moisture absorptionInformation provided by Renegade Materials Corporation.
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
Resin
Moisture Absorption at Equilibrium 1.1 %
1.1 %
Post cured at 350°F
1.2 %
1.2 %
Post cured at 450°F
Mechanical Properties Metric English Comments
Elongation at Break 4.0 %
4.0 %
Resin
Flexural Strength 101 MPa
14600 psi
Resin, RT, Wet
103 MPa
15000 psi
Resin, RT, Dry
1069 MPa
155100 psi
Prepreg, Warp Direction, RT, Dry, Normalized to 60% fiber volume fraction; ASTM D7264
Flexural Modulus 3.17 GPa
460 ksi
Resin, RT, Dry; ASTM D6272
3.17 GPa
460 ksi
Resin, RT, Wet
74.5 GPa
10800 ksi
Prepreg, Warp Direction, RT, Dry; ASTM D7264
Compressive Strength 793 MPa
115000 psi
Prepreg, Warp Direction, RT, Dry; ASTM D6641
Compressive Modulus 65.5 GPa
9500 ksi
Prepreg, Warp Direction, RT, Dry; ASTM D6641
Shear Strength 55.8 MPa
8100 psi
In-Plane, RT, Dry; ASTM D3518
71.7 MPa
10400 psi
Interlaminar, RT, Dry; ASTM D2344
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 166 °C
331 °F
Resin, Wet, Cured at 450°F
227 °C
441 °F
Resin, Dry, Cured at 350°F
Electrical Properties Metric English Comments
Dielectric Constant 2.66

@Frequency 2.00e+9 - 1.80e+10 Hz
2.66

@Frequency 2.00e+9 - 1.80e+10 Hz
Dissipation Factor 0.0050
0.0050