Resinoid 1322 Phenolic Molding, Glass Reinforced

Category	Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Novolac, Glass Filled
Manufacturer	Resinoid
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Resinoid 1322 Phenolic Molding, Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance

Physical Properties	Metric	English	Comments
Density	2.00 g/cc	0.0723 lb/in³	ASTM D792A
Water Absorption	0.10 %	0.10 %	24 hours R.T. ASTM D570
Linear Mold Shrinkage	0.0020 cm/cm	0.0020 in/in	Positive Mold; ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	64.0 MPa	9280 psi	ASTM D651
Flexural Strength	88.0 MPa	12800 psi	ASTM D790
Flexural Modulus	15.0 GPa	2180 ksi	ASTM D790
Compressive Strength	176 MPa	25500 psi	ASTM D695
Izod Impact, Notched	0.473 J/cm	0.886 ft-lb/in	ASTM D256A

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	150 °C	302 °F	UL RTI
Deflection Temperature at 1.8 MPa (264 psi)	288 °C	550 °F	ASTM D648
UL RTI, Electrical	150 °C	302 °F
UL RTI, Mechanical with Impact	150 °C	302 °F
UL RTI, Mechanical without Impact	150 °C	302 °F
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Dielectric Strength	9.40 kV/mm	239 kV/in	Short Time; Dry; ASTM D149
Arc Resistance	190 sec	190 sec	ASTM D495
Comparative Tracking Index	175 - 250 V @Thickness 3.05 mm	175 - 250 V @Thickness 0.120 in	UL PLC 3 (175-250 V)
Hot Wire Ignition, HWI	60 - 120 sec @Thickness 3.05 mm	60 - 120 sec @Thickness 0.120 in	UL PLC 1
High Amp Arc Ignition, HAI	>= 120 arcs @Thickness 3.05 mm	>= 120 arcs @Thickness 0.120 in	UL PLC 0
High Voltage Arc-Tracking Rate, HVTR	0.000 - 10.0 mm/min @Thickness 3.05 mm	0.000 - 0.394 in/min @Thickness 0.120 in	UL PLC 0 (0-10 mm/min)

Processing Properties	Metric	English	Comments
Mold Temperature	155 - 180 °C	311 - 356 °F