Material Notes:
Data provided by the manufacturer.The Resinoid 1300 and 7000 glass fiber reinforced series compounds feature mechanical strength, dimensional stability, electrical insulation, and heat resistance
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ASTM D792A
Water Absorption 0.20 %
0.20 %
24 hours R.T. ASTM D570
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
Positive Mold; ASTM D955
Mechanical Properties Metric English Comments
Flexural Strength 85.0 MPa
12300 psi
ASTM D790
Flexural Modulus 8.90 GPa
1290 ksi
ASTM D790
Compressive Strength 110 MPa
16000 psi
ASTM D695
Izod Impact, Notched 0.341 J/cm
0.639 ft-lb/in
ASTM D256A
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 150 °C
302 °F
UL RTI
Deflection Temperature at 1.8 MPa (264 psi) 275 °C
527 °F
ASTM D648
UL RTI, Electrical 150 °C
302 °F
UL RTI, Mechanical with Impact 150 °C
302 °F
UL RTI, Mechanical without Impact 150 °C
302 °F
Electrical Properties Metric English Comments
Dielectric Strength 12.8 kV/mm
325 kV/in
Short Time; Dry; ASTM D149
Arc Resistance 130 sec
130 sec
ASTM D495
Comparative Tracking Index 175 - 250 V

@Thickness 3.05 mm
175 - 250 V

@Thickness 0.120 in
UL PLC 3 (175-250 V)
Hot Wire Ignition, HWI >= 0.00 sec

@Thickness 3.05 mm
>= 0.00 sec

@Thickness 0.120 in
UL PLC 0
High Amp Arc Ignition, HAI 15 - 29 arcs

@Thickness 6.10 mm
15 - 29 arcs

@Thickness 0.240 in
UL PLC 3, 15-29 arcs
High Voltage Arc-Tracking Rate, HVTR 0.000 - 10.0 mm/min

@Thickness 6.10 mm
0.000 - 0.394 in/min

@Thickness 0.240 in
UL PLC 0 (0-10 mm/min)
Processing Properties Metric English Comments
Mold Temperature 155 - 180 °C