SABIC 6318B Linear Low Density Polyethylene for Cast Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade |
| Manufacturer | SABIC |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC 6318B Linear Low Density Polyethylene for Cast Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: 6318B is a hexene copolymer Linear Low Density Polyethylene grade designed to provide easy processability and specially formulated for optimum thermal stability at high processing temperatures used during the production of Cast films. Films produced using this resin give excellent optical properties, puncture resistance and tear strength.Typical Applications: It is recommended for pellet wrap (pre-stretch), high performance draw down films and other general purpose applications where high strength is required.Information provided by SABIC.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | load density; ASTM D1505 |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 2.8 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.8 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 13.0 MPa | 1890 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 |
| Elmendorf Tear Strength MD | 200 g | 200 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 800 g | 800 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 6.67 g/micron | 169 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 26.67 g/micron | 677.4 g/mil | ASTM D1922 |
| Dart Drop Total Energy | 640 J/cm | 1.20 ft-lb/mil | Puncture Resistance; SABIC Method |
| Dart Drop | 4.00 g/micron | 102 g/mil | ASTM D1709 |
| Dart Drop Test | 120 g | 0.265 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 33.0 MPa | 4790 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 24.0 MPa | 3480 psi | ASTM D882 |
| 1% Secant Modulus, MD | 180 MPa | 26100 psi | ASTM D882 |
| 1% Secant Modulus, TD | 190 MPa | 27600 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 92 % | 92 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 265 - 300 °C | 509 - 572 °F | |
| Roll Temperature | 20.0 °C | 68.0 °F |