SABIC BM6246LS High Density Polyethylene for Blow Molding

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer SABIC
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC BM6246LS High Density Polyethylene for Blow Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: BM6246LS grade is a medium molecular weight High Density Polyethylene homopolymer for blow molding applications. It is primarily designed for imparting high rigidity, toughness and good processability. These unique properties offer the possibility to reduce weight at very good top load strength.Typical Applications: BM6246LS resin is primarily intended for blow molding bottles for the food and beverage industry. This grade is intended to meet customer specifications in respect to purity, healthiness and organoleptics. It can be used for milk, fruit juice and other dairy products. It can also be used in other thin-walled parts and profile extrusions. The product is not recommended for packaging environmentally active materials such as soaps, detergents, shampoos, etc.Information provided by SABIC.
Physical Properties Metric English Comments
Density 0.961 g/cc
0.0347 lb/in³
ASTM D1505
ESCR 100% Igepal® 24 hour
24 hour
F50; ASTM D1693B
ESCR 10% Igepal® 16 hour
16 hour
F50; ASTM D1693B
Melt Flow 0.70 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.70 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
2.8 g/10 min

@Load 5.00 kg,
Temperature 190 °C
2.8 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ASTM D1238
46 g/10 min

@Load 21.6 kg,
Temperature 190 °C
46 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 66
66
ASTM D2240
Tensile Strength at Break 18.0 MPa
2610 psi
ASTM D638
Tensile Strength, Yield 30.0 MPa
4350 psi
ASTM D638
Elongation at Break 500 %
500 %
ASTM D638
Flexural Strength 28.0 MPa
4060 psi
ASTM D790
Flexural Modulus 1.10 GPa
160 ksi
ASTM D790
1% Secant Modulus >= 1000 MPa
>= 145000 psi
ASTM D638
Izod Impact, Notched 1.50 J/cm
2.81 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Vicat Softening Point 127 °C
261 °F
ASTM D1525
Brittleness Temperature <= -75.0 °C
<= -103 °F
ASTM D746
Processing Properties Metric English Comments
Melt Temperature 190 - 210 °C
374 - 410 °F