SABIC F04660 High Density Polyethylene for Blown Film Applications

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer	SABIC
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC F04660 High Density Polyethylene for Blown Film Applications.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: F04660 is a homopolymer HDPE film grade with excellent processability and high stiffness. It has good moisture barrier properties and can be blended with LDPE and LLDPE to improve film strength and rigidity.Typical Applications: F04660 is recommended for applications where high stiffness is required. It can be used in the middle layer in a coex structure or blended with LDPE and LLDPE to increase stiffness and mechanical properties. It has excellent water vapor barrier properties required for certain foods packaging.Information provided by SABIC.

Physical Properties	Metric	English	Comments
Density	0.961 g/cc	0.0347 lb/in³	ASTM D1505
Thickness	25.0 microns	0.984 mil
Melt Flow	0.70 g/10 min @Load 2.16 kg, Temperature 190 °C	0.70 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
	46 g/10 min @Load 21.6 kg, Temperature 190 °C	46 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	490 %	490 %	ASTM D882
Film Elongation at Break, TD	3.0 %	3.0 %	ASTM D882
Elmendorf Tear Strength MD	10 g	10 g	ASTM D1922
Elmendorf Tear Strength TD	800 g	800 g	ASTM D1922
Elmendorf Tear Strength, MD	0.400 g/micron	10.2 g/mil	ASTM D1922
Elmendorf Tear Strength, TD	32.0 g/micron	813 g/mil	ASTM D1922
Dart Drop Test	<= 20.0 g	<= 0.0441 lb	ASTM D1709
Film Tensile Strength at Break, MD	67.0 MPa	9720 psi	ASTM D882
Film Tensile Strength at Break, TD	37.0 MPa	5370 psi	ASTM D882
1% Secant Modulus, MD	1250 MPa	181000 psi	ASTM D882
1% Secant Modulus, TD	1700 MPa	247000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Vicat Softening Point	129 °C	264 °F	ASTM D1525

Processing Properties	Metric	English	Comments
Melt Temperature	200 - 235 °C	392 - 455 °F
Blow-up Ratio (BUR)	2.5	2.5