SABIC HP4023W Low Density Polyethylene for Blown Film
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade |
| Manufacturer | SABIC |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC HP4023W Low Density Polyethylene for Blown Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: HP4023W is a Low Density Polyethylene grade suitable for producing general purpose films and contains slip and antiblock additives. It yields excellent processability with good mechanical properties.Typical Applications: HP4023W can be used for high clarity laundry bags, textile wrapping films, produce bags and zip lock bags.Information provided by SABIC.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 4.0 g/10 min @Load 21.6 kg, Temperature 190 °C |
4.0 g/10 min @Load 47.6 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 7.00 MPa | 1020 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.00 MPa | 1020 psi | ASTM D882 |
| Film Elongation at Break, MD | 270 % | 270 % | ASTM D882 |
| Film Elongation at Break, TD | 540 % | 540 % | ASTM D882 |
| Elmendorf Tear Strength MD | 150 g | 150 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 120 g | 120 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 5.00 g/micron | 127 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 4.00 g/micron | 102 g/mil | ASTM D1922 |
| Dart Drop | 2.00 g/micron | 50.8 g/mil | ASTM D1709 |
| Dart Drop Test | 60.0 g | 0.132 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 18.0 MPa | 2610 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 15.0 MPa | 2180 psi | ASTM D882 |
| 1% Secant Modulus, MD | 60.0 MPa | 8700 psi | ASTM D882 |
| 1% Secant Modulus, TD | 170 MPa | 24700 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 91.0 °C | 196 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 7.0 % | 7.0 % | ASTM D1003 |
| Gloss | 75 % | 75 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 160 - 175 °C | 320 - 347 °F | |
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 |