SABIC Innovative Plastics Cycolac® FR15U ABS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® FR15U ABS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
CYCOLAC FR15U is a flame retardant ABS with good processability and good indoor UV properties.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.200 % | 0.200 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | on Tensile Bar; SABIC Method |
| Melt Flow | 7.0 g/10 min @Load 5.00 kg, Temperature 220 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 428 °F |
ISO 1133 |
| Melt Index of Compound | 40 g/10 min @Load 10.0 kg, Temperature 220 °C |
40 g/10 min @Load 22.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 22 % | 22 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.21 GPa | 321 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 63.0 MPa | 9140 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.26 GPa | 328 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft²-°F | ISO 8302 |
| Vicat Softening Point | 92.0 °C | 198 °F | Rate B/50; ISO 306 |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 |
| 5VA @Thickness 2.80 mm |
5VA @Thickness 0.110 in |
UL 94 | |
| Oxygen Index | 26 % | 26 % | ISO 4589 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Dielectric Strength | 20.0 kV/mm @Thickness 3.20 mm |
508 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Packaging JGR-154A Polyvinyl Chloride, Rigid (PVC, Rigid)
- PolyOne Maxxam™ NT-818.G002-8000 Polypropylene, Unspecified (PP, Unspecified)
- Potters Industries Conduct-O-Fil® SG05TF40 Silver-coated Sub-10 micron Particles
- Michelman® Michem® Prime 4990R Ethylene acrylic acid dispersion
- Lotte Chemical Titan TITANPRO® PM430 Polypropylene homopolymer
- Karina 822-IS-SD Clear PVC Compound
- Taiwan PU Corporation TPU-C75 General Grade, Calender Molding Polyester Base TPU
- ExxonMobil Isopar™ M (EU) Isoparaffin Fluid
- Arlon 44580R010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Chesterton 652 Pneumatic Lubricant & Conditioner
Copyright © lookpolymers.com All Rights Reserved