SABIC Innovative Plastics Cycolac® INP564 ABS+SAN

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycolac®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycolac® INP564 ABS+SAN.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
SABIC INP564 provides compatibility with a wider range of ABS grades than many color concentrate bases; allows better dispersion than pellets; allows concentrate manufacturers to produce both pelletized and dry blend concentrate; provides a base resin with less heat history than pellets; suitable for direct weather exposure; can be used in all SAN applications where a fine particle size is desired
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
ASTM D792
Density 1.07 g/cc
0.0387 lb/in³
ISO 1183
Melt Flow 37.8 g/10 min

@Load 3.80 kg,
Temperature 230 °C
37.8 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
78 g/10 min

@Load 10.0 kg,
Temperature 220 °C
78 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 123
123
ASTM D785
Tensile Strength at Break 53.0 MPa
7690 psi
Type I, 5 mm/min; ASTM D638
54.0 MPa
7830 psi
50 mm/min; ISO 527
Tensile Strength, Yield 52.0 MPa
7540 psi
Type I, 5 mm/min; ASTM D638
54.0 MPa
7830 psi
50 mm/min; ISO 527
Elongation at Break 1.2 %
1.2 %
50 mm/min; ISO 527
1.7 %
1.7 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 1.2 %
1.2 %
50 mm/min; ISO 527
1.6 %
1.6 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.84 GPa
557 ksi
1 mm/min; ISO 527
3.89 GPa
564 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 65.0 MPa
9430 psi
2 mm/min; ISO 178
82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.46 GPa
502 ksi
2 mm/min; ISO 178
3.72 GPa
540 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.140 J/cm
0.262 ft-lb/in
ASTM D256
0.220 J/cm

@Temperature -30.0 °C
0.412 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 1.00 kJ/m²
0.476 ft-lb/in²
80*10*4; ISO 180/1A
2.00 kJ/m²

@Temperature -30.0 °C
0.952 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.100 J/cm²
0.476 ft-lb/in²
ISO 179/2C
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 95.0 °C

@Thickness 3.20 mm
203 °F

@Thickness 0.126 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 85.0 °C
185 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
83.0 °C

@Thickness 3.20 mm
181 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 101 °C
214 °F
Rate B/50; ISO 306
104 °C
219 °F
Rate B/120; ISO 306