SABIC Innovative Plastics Cycoloy® C6200 PC+ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C6200 PC+ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
CYCOLOY C6200 is a non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs. C6200 has improved processing window and edge crack resistance.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.60 %

@Temperature 23.0 °C
0.60 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
on tensile bar; SABIC Method
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 260 °C
13 g/10 min

@Load 4.76 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 122
122
ISO 2039-2
Hardness, H358/30 116 MPa
16800 psi
ISO 2039-1
Tensile Strength at Break 40.0 MPa
5800 psi
5 mm/min; ISO 527
50.0 MPa
7250 psi
50 mm/min; ISO 527
Tensile Strength, Yield 50.0 MPa
7250 psi
5 mm/min; ISO 527
60.0 MPa
8700 psi
50 mm/min; ISO 527
Elongation at Break >= 50 %
>= 50 %
50 mm/min; ISO 527
57 %
57 %
5 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
5 mm/min; ISO 527
4.0 %
4.0 %
50 mm/min; ISO 527
Tensile Modulus 2.80 GPa
406 ksi
1 mm/min; ISO 527
Flexural Yield Strength 98.0 MPa
14200 psi
2 mm/min; ISO 178
Flexural Modulus 2.80 GPa
406 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
15.0 kJ/m²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
15.0 kJ/m²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles 82

@Load 1.00 kg
82

@Load 2.20 lb
CS-17; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Hot Ball Pressure Test <= 85.0 °C
<= 185 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 96.0 °C
205 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
183 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 98.0 °C
208 °F
Rate B/50; ISO 306
102 °C
216 °F
Rate B/120; ISO 306
UL RTI, Electrical 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical with Impact 75.0 °C
167 °F
UL 746B
UL RTI, Mechanical without Impact 85.0 °C
185 °F
UL 746B
Flammability, UL94 HB

@Thickness 0.700 mm
HB

@Thickness 0.0276 in
UL 94
V-1

@Thickness 1.20 mm
V-1

@Thickness 0.0472 in
UL 94
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
5VB

@Thickness 2.00 mm
5VB

@Thickness 0.0787 in
UL 94
5VA

@Thickness 3.40 mm
5VA

@Thickness 0.134 in
UL 94
Oxygen Index 32 %
32 %
LOI; ISO 4589
Glow Wire Test 960 °C

@Thickness 3.20 mm
1760 °F

@Thickness 0.126 in
Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.7

@Frequency 1.00e+6 Hz
2.7

@Frequency 1.00e+6 Hz
IEC 60250
2.8

@Frequency 50.0 - 60.0 Hz
2.8

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
25.0 kV/mm

@Thickness 1.60 mm
635 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
35.0 kV/mm

@Thickness 0.800 mm
889 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Dissipation Factor 0.0040

@Frequency 50.0 - 60.0 Hz
0.0040

@Frequency 50.0 - 60.0 Hz
IEC 60250
0.0080

@Frequency 1.00e+6 Hz
0.0080

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 250 - 400 V
250 - 400 V
PLC code 2; UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASSES
IEC 60695-10-2