SABIC Innovative Plastics Cycoloy® C6840 PC+ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C6840 PC+ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cycoloy* C6840 resin is an injection moldable, flame retardant PC/ABS blend. It contains non-chlorinated & non-brominated flame retardant systems intended to meet governmental regulations and various voluntary environmental labels. Key features of Cycoloy C6840 resin including very good flow, balanced impact property, heat resistance, hydrolytic stability and all color options make this grade an ideal candidate for thin wall applications.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %
0.20 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 26 g/10 min

@Load 2.16 kg,
Temperature 260 °C
26 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 23 g/10 min

@Load 2.16 kg,
Temperature 260 °C
23 g/10 min

@Load 4.76 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
Type I, 50 mm/min; ASTM D638
44.0 MPa
6380 psi
50 mm/min; ISO 527
Tensile Strength, Yield 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
56.0 MPa
8120 psi
50 mm/min; ISO 527
Elongation at Break 51 %
51 %
Type I, 50 mm/min; ASTM D638
60 %
60 %
50 mm/min; ISO 527
Elongation at Yield 3.6 %
3.6 %
Type I, 50 mm/min; ASTM D638
4.0 %
4.0 %
50 mm/min; ISO 527
Tensile Modulus 2.50 GPa
363 ksi
1 mm/min; ISO 527
2.58 GPa
374 ksi
5 mm/min; ASTM D638
Flexural Strength 90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Yield Strength 92.0 MPa
13300 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.60 GPa
377 ksi
2 mm/min; ISO 178
Izod Impact, Notched 5.00 J/cm
9.37 ft-lb/in
ASTM D256
1.10 J/cm

@Temperature -30.0 °C
2.06 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
80*10*3; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 40.0 J

@Temperature 23.0 °C
29.5 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 60.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
33.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
75.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
41.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Thermal Conductivity 0.200 W/m-K
1.39 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 89.0 °C

@Thickness 3.20 mm
192 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
85.0 °C

@Thickness 3.20 mm
185 °F

@Thickness 0.126 in
unannealed; ASTM D648
85.0 °C

@Thickness 6.40 mm
185 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 93.0 °C
199 °F
Rate B/50; ASTM D1525
93.0 °C
199 °F
Rate B/50; ISO 306
96.0 °C
205 °F
Rate B/120; ISO 306
UL RTI, Electrical 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical with Impact 60.0 °C
140 °F
UL 746B
UL RTI, Mechanical without Impact 60.0 °C
140 °F
UL 746B
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
5VB

@Thickness 2.00 mm
5VB

@Thickness 0.0787 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Strength 17.0 kV/mm

@Thickness 3.20 mm
432 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
25.0 kV/mm

@Thickness 1.60 mm
635 kV/in

@Thickness 0.0630 in
in oil; IEC 60243-1
35.0 kV/mm

@Thickness 0.800 mm
889 kV/in

@Thickness 0.0315 in
in oil; IEC 60243-1
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASSES
IEC 60695-10-2