SABIC Innovative Plastics Cycoloy® C7230P PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® C7230P PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cycoloy* C7230P resin is a mineral filled, flame retardant PC/ABS. Good stiffness combined with balanced flow and impact performance, makes it a good candidate for various applications.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Density 1.30 g/cc
0.0470 lb/in³
ISO 1183
Moisture Absorption 0.0400 %
0.0400 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.090 %
0.090 %
ISO 62
Linear Mold Shrinkage, Flow 0.0025 - 0.0035 cm/cm

@Thickness 3.20 mm
0.0025 - 0.0035 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 13 g/10 min

@Load 2.16 kg,
Temperature 260 °C
13 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 9.0 g/10 min

@Load 2.16 kg,
Temperature 260 °C
9.0 g/10 min

@Load 4.76 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 35.0 MPa
5080 psi
50 mm/min; ISO 527
45.0 MPa
6530 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 55.0 MPa
7980 psi
50 mm/min; ISO 527
58.0 MPa
8410 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 30 %
30 %
50 mm/min; ISO 527
32 %
32 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 3.8 %
3.8 %
50 mm/min; ISO 527
4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 5.20 GPa
754 ksi
5 mm/min; ASTM D638
5.58 GPa
809 ksi
1 mm/min; ISO 527
Flexural Yield Strength 98.0 MPa
14200 psi
1.3 mm/min, 50 mm span; ASTM D790
99.0 MPa
14400 psi
2 mm/min; ISO 178
Flexural Modulus 4.53 GPa
657 ksi
1.3 mm/min, 50 mm span; ASTM D790
4.58 GPa
664 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.690 J/cm
1.29 ft-lb/in
ASTM D256
0.550 J/cm

@Temperature -30.0 °C
1.03 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 42.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
23.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
42.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
23.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 49.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
59.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
32.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 89.0 °C
192 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
88.0 °C

@Thickness 3.20 mm
190 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 107 °C
225 °F
Rate B/50; ISO 306
108 °C
226 °F
Rate B/50; ASTM D1525
110 °C
230 °F
Rate B/120; ISO 306
Flammability, UL94 V-0

@Thickness 1.20 mm
V-0

@Thickness 0.0472 in
UL 94
5VB

@Thickness 2.00 mm
5VB

@Thickness 0.0787 in
UL 94