SABIC Innovative Plastics Cycoloy® CY5105 PC+ABS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CY5105 PC+ABS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering excellent flow / impact balance for large size applicationsThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.60 %

@Temperature 23.0 °C
 0.60 %

@Temperature 73.4 °F
 ISO 62
Melt Flow 23 g/10 min

@Load 2.16 kg,
Temperature 260 °C
 23 g/10 min

@Load 4.76 lb,
Temperature 500 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
50 mm/min; ISO 527
47.0 MPa
6820 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D 638
62.0 MPa
8990 psi
50 mm/min; ISO 527
Elongation at Break 35 %
35 %
50 mm/min; ISO 527
55 %
55 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527
4.1 %
4.1 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.75 GPa
399 ksi
5 mm/min; ASTM D 638
2.75 GPa
399 ksi
1 mm/min; ISO 527
Flexural Yield Strength 94.0 MPa
13600 psi
2 mm/min; ISO 178
Flexural Modulus 2.45 GPa
355 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.750 J/cm

@Temperature -30.0 °C
 1.41 ft-lb/in

@Temperature -22.0 °F
 ASTM D 256
3.50 J/cm

@Temperature 23.0 °C
 6.56 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 80*10*3; ISO 180/1A
20.0 kJ/m²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
30.0 kJ/m²

@Temperature 23.0 °C
 14.3 ft-lb/in²

@Temperature 73.4 °F
 80*10*3; ISO 180/1A
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
2.20 J/cm²

@Temperature 23.0 °C
 10.5 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
3.00 J/cm²

@Temperature 23.0 °C
 14.3 ft-lb/in²

@Temperature 73.4 °F
 V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 44.4 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 104 °C
219 °F
Rate B/50; ISO 306
105 °C
221 °F
Rate B/120; ISO 306
Flammability, UL94 V-1

@Thickness 1.50 mm
 V-1

@Thickness 0.0591 in
 UL 94
V-0

@Thickness 2.00 mm
 V-0

@Thickness 0.0787 in
 UL 94
Oxygen Index 31 %
31 %
LOI; ISO 4589
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.9

@Frequency 50.0 - 60.0 Hz
 2.9

@Frequency 50.0 - 60.0 Hz
 IEC 60250
Dissipation Factor 0.0070

@Frequency 1.00e+6 Hz
 0.0070

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 250 - 400 V
250 - 400 V
PLC code 2; UL 746A