SABIC Innovative Plastics Cycoloy® CY6310 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® CY6310 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow / impact balance for a wide variety of thin wall or large size applications including business equipment, enclosures, among others.
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D792
Density 1.16 g/cc
0.0419 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.60 %
0.60 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 16 g/10 min

@Load 2.16 kg,
Temperature 250 °C
16 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ASTM D1238
20 g/10 min

@Load 2.16 kg,
Temperature 260 °C
20 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 19 g/10 min

@Load 2.16 kg,
Temperature 260 °C
19 g/10 min

@Load 4.76 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
Type I, 50 mm/min; ASTM D638
51.0 MPa
7400 psi
50 mm/min; ISO 527
Tensile Strength, Yield 63.0 MPa
9140 psi
50 mm/min; ISO 527
63.0 MPa
9140 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break >= 50 %
>= 50 %
50 mm/min; ISO 527
>= 50 %
>= 50 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.2 %
4.2 %
Type I, 50 mm/min; ASTM D638
4.4 %
4.4 %
50 mm/min; ISO 527
Tensile Modulus 2.70 GPa
392 ksi
1 mm/min; ISO 527
2.70 GPa
392 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 91.0 MPa
13200 psi
2 mm/min; ISO 178
101 MPa
14600 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.65 GPa
384 ksi
2 mm/min; ISO 178
2.70 GPa
392 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 6.00 J/cm
11.2 ft-lb/in
ASTM D256
1.15 J/cm

@Temperature -30.0 °C
2.15 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
80*10*3; ISO 180/1A
13.0 kJ/m²

@Temperature -30.0 °C
6.19 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 5.50 J/cm²
26.2 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
1.40 J/cm²

@Temperature -30.0 °C
6.66 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 65.0 J

@Temperature 23.0 °C
47.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 105 J
77.4 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 68.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
37.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
68.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
37.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Hot Ball Pressure Test <= 95.0 °C
<= 203 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 100 °C

@Thickness 3.20 mm
212 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
88.0 °C

@Thickness 3.20 mm
190 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 109 °C
228 °F
Rate B/50; ASTM D1525
109 °C
228 °F
Rate B/50; ISO 306
111 °C
232 °F
Rate B/120; ISO 306
UL RTI, Electrical 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical with Impact 85.0 °C
185 °F
UL 746B
UL RTI, Mechanical without Impact 85.0 °C
185 °F
UL 746B
Flammability, UL94 V-2

@Thickness 0.750 mm
V-2

@Thickness 0.0295 in
UL 94 by SABIC-IP
V-2

@Thickness 0.750 mm
V-2

@Thickness 0.0295 in
UL 94
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94 by SABIC-IP
5VB

@Thickness 2.30 mm
5VB

@Thickness 0.0906 in
UL 94
5VB

@Thickness 2.30 mm
5VB

@Thickness 0.0906 in
UL 94 by SABIC-IP
5VA

@Thickness 2.90 mm
5VA

@Thickness 0.114 in
UL 94 by SABIC-IP
5VA

@Thickness 2.90 mm
5VA

@Thickness 0.114 in
UL 94
Oxygen Index 30 %
30 %
ISO 4589
Glow Wire Test 960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Comparative Tracking Index 575 V
575 V
IEC 60112
Hot Wire Ignition, HWI 15 - 30 sec
15 - 30 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C Pass
IEC 60695-10-2