SABIC Innovative Plastics Cycoloy® RCY6013 PC+ABS (Asia Pacific)

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Cycoloy®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Cycoloy® RCY6013 PC+ABS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Cycoloy* RCY6013 resin is an injection moldable high flow PC/ABS blend with non-brominated and non-chlorinated flame retardant. It contains 30% post consumer recycle content with a UL-94 V0 @ 1.5 mm. Developed for wide variety of applications that require high flow and moderate impact performance. Limited availability and restricted color only.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 34 g/10 min

@Load 2.16 kg,
Temperature 260 °C
34 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 45.0 MPa
6530 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 60.0 MPa
8700 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 34 %
34 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 3.6 %
3.6 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.60 GPa
377 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 92.0 MPa
13300 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.50 GPa
363 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.900 J/cm
1.69 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
80*10*3; ISO 180/1A
Dart Drop, Total Energy 18.0 J

@Temperature 23.0 °C
13.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.0 µm/m-°C

@Temperature -40.0 - 60.0 °C
39.4 µin/in-°F

@Temperature -40.0 - 140 °F
ASTM E 831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 60.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 140 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 92.0 °C

@Thickness 6.40 mm
198 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 76.0 °C

@Thickness 3.20 mm
169 °F

@Thickness 0.126 in
unannealed; ASTM D648
82.0 °C

@Thickness 6.40 mm
180 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 92.0 °C
198 °F
Rate B/50; ASTM D1525
Flammability, UL94 V-1

@Thickness 1.20 mm
V-1

@Thickness 0.0472 in
UL 94
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
UL 94