SABIC Innovative Plastics EXTEM UH1016 TPI Blend (Asia Pacific)

Category Polymer , Thermoplastic , Polyimide, Thermoplastic
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Extem
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics EXTEM UH1016 TPI Blend (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High heat amorphous TPI Blend, Chemical Resistant, High Flow
Physical Properties Metric English Comments
Specific Gravity 1.37 g/cc
1.37 g/cc
ASTM D792
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 0.60 %

@Time 173000 sec
0.60 %

@Time 48.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm

@Thickness 3.20 mm
0.0080 - 0.010 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 12 g/10 min

@Load 6.60 kg,
Temperature 400 °C
12 g/10 min

@Load 14.6 lb,
Temperature 752 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
5 mm/min; ISO 527
110 MPa
16000 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 112 MPa
16200 psi
5 mm/min; ISO 527
120 MPa
17400 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 10 %
10 %
Type I, 5 mm/min; ASTM D638
17 %
17 %
5 mm/min; ISO 527
Elongation at Yield 9.0 %
9.0 %
Type I, 5 mm/min; ASTM D638
9.0 %
9.0 %
5 mm/min; ISO 527
Tensile Modulus 3.50 GPa
508 ksi
1 mm/min; ISO 527
3.80 GPa
551 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 155 MPa
22500 psi
2 mm/min; ISO 178
175 MPa
25400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.00 GPa
435 ksi
2 mm/min; ISO 178
3.52 GPa
511 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.600 J/cm
1.12 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
Charpy Impact, Notched 2.20 J/cm²
10.5 ft-lb/in²
ISO 179/2C
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 46.0 µm/m-°C

@Temperature 23.0 - 150 °C
25.6 µin/in-°F

@Temperature 73.4 - 302 °F
ASTM E 831
CTE, linear, Transverse to Flow 47.0 µm/m-°C

@Temperature 23.0 - 150 °C
26.1 µin/in-°F

@Temperature 73.4 - 302 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 263 °C

@Thickness 3.20 mm
505 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 231 °C
448 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
240 °C

@Thickness 3.20 mm
464 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 257 °C
495 °F
Rate B/50; ASTM D1525
261 °C
502 °F
Rate B/50; ISO 306
263 °C
505 °F
Rate B/120; ISO 306