SABIC Innovative Plastics GELOY XTPMFR10 ASA+PC (Asia Pacific)

Category Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics GELOY XTPMFR10 ASA+PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Improved ASA/PC blend for high flow, 1.0mm V0 applications. Improved UV performance aesthetically and physically compared to alternatives.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Viscosity 105000 cP
105000 cP
Melt Viscosity, 260°C, 1500 sec-1; ISO 11443
Melt Flow 29 g/10 min

@Load 2.16 kg,
Temperature 260 °C
29 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Melt Index of Compound 30 g/10 min

@Load 2.16 kg,
Temperature 260 °C
30 g/10 min

@Load 4.76 lb,
Temperature 500 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.0 MPa
6380 psi
Type I, 50 mm/min; ASTM D638
47.0 MPa
6820 psi
50 mm/min; ISO 527
Tensile Strength, Yield 64.0 MPa
9280 psi
Type I, 50 mm/min; ASTM D638
66.0 MPa
9570 psi
50 mm/min; ISO 527
Elongation at Break 21 %
21 %
50 mm/min; ISO 527
43.5 %
43.5 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.0 %
4.0 %
Type I, 50 mm/min; ASTM D638
4.0 %
4.0 %
50 mm/min; ISO 527
Tensile Modulus 2.68 GPa
389 ksi
1 mm/min; ISO 527
2.70 GPa
392 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 97.0 MPa
14100 psi
1.3 mm/min, 50 mm span; ASTM D790
97.0 MPa
14100 psi
2 mm/min; ISO 178
Flexural Modulus 2.55 GPa
370 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.72 GPa
395 ksi
2 mm/min; ISO 178
Izod Impact, Notched 3.30 J/cm
6.18 ft-lb/in
ASTM D256
0.720 J/cm

@Temperature 0.000 °C
1.35 ft-lb/in

@Temperature 32.0 °F
ASTM D256
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1A
12.0 kJ/m²

@Temperature 0.000 °C
5.71 ft-lb/in²

@Temperature 32.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.30 J/cm²
6.19 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 50.0 J

@Temperature 23.0 °C
36.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 85.0 J
62.7 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 62.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
34.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 62.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
34.4 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
63.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
35.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 90.0 °C
194 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C
178 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
80.0 °C

@Thickness 3.20 mm
176 °F

@Thickness 0.126 in
unannealed; ASTM D648
90.0 °C

@Thickness 6.40 mm
194 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 96.0 °C
205 °F
Rate B/50; ISO 306
97.0 °C
207 °F
Rate B/50; ASTM D1525
98.0 °C
208 °F
Rate B/120; ISO 306
Flammability, UL94 V-1

@Thickness 0.800 mm
V-1

@Thickness 0.0315 in
UL 94
V-0

@Thickness 1.00 mm
V-0

@Thickness 0.0394 in
UL 94
5VB

@Thickness 2.00 mm
5VB

@Thickness 0.0787 in
UL 94
Glow Wire Test 775 °C
1430 °F
IEC 60695-2-13
825 °C
1520 °F
IEC 60695-2-13
875 °C
1610 °F
IEC 60695-2-13
960 °C

@Thickness 0.800 mm
1760 °F

@Thickness 0.0315 in
IEC 60695-2-12
Users viewing this material also viewed the following: