SABIC Innovative Plastics Geloy FXW710SK ASA/SAN (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ASA Polymer , SAN Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Geloy FXW710SK ASA/SAN (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
GELOY FXW710SK is an ASA/SAN injection moulding grade. It is suitable for those applications that require sparkle colour effects.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Density 1.09 g/cc
0.0394 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.55 %

@Temperature 23.0 °C
0.55 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
on tensile bar; SABIC Method
Melt Flow 7.0 g/10 min

@Load 10.0 kg,
Temperature 220 °C
7.0 g/10 min

@Load 22.0 lb,
Temperature 428 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
8.0 g/10 min

@Load 5.00 kg,
Temperature 260 °C
8.0 g/10 min

@Load 11.0 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 95
95
ISO 2039-2
Hardness, H358/30 70.0 MPa
10200 psi
ISO 2039-1
Tensile Strength at Break 30.0 MPa
4350 psi
50 mm/min; ISO 527
Tensile Strength, Yield 38.0 MPa
5510 psi
50 mm/min; ISO 527
Elongation at Break 4.0 %
4.0 %
50 mm/min; ISO 527
Elongation at Yield 2.5 %
2.5 %
50 mm/min; ISO 527
Tensile Modulus 1.90 GPa
276 ksi
1 mm/min; ISO 527
Flexural Yield Strength 50.0 MPa
7250 psi
2 mm/min; ISO 178
Flexural Modulus 1.90 GPa
276 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 0.400 J/cm²

@Temperature -30.0 °C
1.90 ft-lb/in²

@Temperature -22.0 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
1.20 J/cm²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Taber Abrasion, mg/1000 Cycles 155

@Load 1.00 kg
155

@Load 2.20 lb
CS-17; SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
50.0 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature 23.0 - 60.0 °C
55.6 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Thermal Conductivity 0.210 W/m-K
1.46 BTU-in/hr-ft²-°F
ISO 8302
Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C
190 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
Vicat Softening Point 86.0 °C
187 °F
Rate B/50; ISO 306
91.0 °C
196 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.00 mm
HB

@Thickness 0.0394 in
UL 94 by SABIC-IP
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
2nd value; UL 94 by SABIC-IP
Oxygen Index 19 %
19 %
LOI; ISO 4589
Glow Wire Test 750 °C

@Thickness 3.20 mm
1380 °F

@Thickness 0.126 in
Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
IEC 60250
5.2

@Frequency 50.0 - 60.0 Hz
5.2

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
406 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.026

@Frequency 1.00e+6 Hz
0.026

@Frequency 1.00e+6 Hz
IEC 60250
0.15

@Frequency 50.0 - 60.0 Hz
0.15

@Frequency 50.0 - 60.0 Hz
IEC 60250
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASSES
IEC 60695-10-2