SABIC Innovative Plastics Geloy XTPM307 ASA+PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Geloy XTPM307 ASA+PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
XTPM307 is a high heat resistant PC/ASA with improved processing stability over HRA150. Typical values measured on natural material.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % @Temperature 23.0 °C |
0.60 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 5.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
5.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 6.0 g/10 min @Load 5.00 kg, Temperature 240 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 464 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| 16 g/10 min @Load 5.00 kg, Temperature 260 °C |
16 g/10 min @Load 11.0 lb, Temperature 500 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| 50 g/10 min @Load 10.0 kg, Temperature 260 °C |
50 g/10 min @Load 22.0 lb, Temperature 500 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 |
| 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 | |
| 62.0 MPa | 8990 psi | Type I, 5 mm/min; ASTM D 638 | |
| 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | Type I, 5 mm/min; ASTM D 638 |
| 53.0 MPa | 7690 psi | 5 mm/min; ISO 527 | |
| 57.0 MPa | 8270 psi | Type I, 50 mm/min; ASTM D 638 | |
| 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | >= 100 % | >= 100 % | Type I, 50 mm/min; ASTM D 638 |
| >= 100 % | >= 100 % | Type I, 5 mm/min; ASTM D 638 | |
| >= 100 % | >= 100 % | 5 mm/min; ISO 527 | |
| >= 100 % | >= 100 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 4.7 % | 4.7 % | 5 mm/min; ISO 527 |
| 4.7 % | 4.7 % | 50 mm/min; ISO 527 | |
| 4.8 % | 4.8 % | Type I, 50 mm/min; ASTM D 638 | |
| 4.8 % | 4.8 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.28 GPa | 331 ksi | 5 mm/min; ASTM D 638 |
| 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 84.0 MPa | 12200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.21 GPa | 321 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 2.05 J/cm @Temperature -20.0 °C |
3.84 ft-lb/in @Temperature -4.00 °F |
ASTM D 256 |
| 2.45 J/cm @Temperature -10.0 °C |
4.59 ft-lb/in @Temperature 14.0 °F |
ASTM D 256 | |
| 5.95 J/cm @Temperature 0.000 °C |
11.1 ft-lb/in @Temperature 32.0 °F |
ASTM D 256 | |
| 6.40 J/cm @Temperature 23.0 °C |
12.0 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 17.0 kJ/m² @Temperature -30.0 °C |
8.09 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 20.0 kJ/m² @Temperature -20.0 °C |
9.52 ft-lb/in² @Temperature -4.00 °F |
80*10*4; ISO 180/1A | |
| 26.0 kJ/m² @Temperature -10.0 °C |
12.4 ft-lb/in² @Temperature 14.0 °F |
80*10*4; ISO 180/1A | |
| 46.0 kJ/m² @Temperature 0.000 °C |
21.9 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 59.0 kJ/m² @Temperature 23.0 °C |
28.1 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Impact Test | 120 J | 88.5 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Hot Ball Pressure Test | <= 105 °C | <= 221 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 103 °C | 217 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 116 °C | 241 °F | Rate B/50; ISO 306 |
| 118 °C | 244 °F | Rate B/120; ISO 306 | |
| 138 °C | 280 °F | Rate A/50; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.20e+15 ohm-cm | 4.20e+15 ohm-cm | ASTM D 257 |
| Surface Resistance | 1.50e+16 ohm | 1.50e+16 ohm | ASTM D 257 |
| Dielectric Strength | 27.5 kV/mm @Thickness 1.60 mm |
699 kV/in @Thickness 0.0630 in |
in oil; ASTM D 149 |
| Dissipation Factor | 0.0153 @Frequency 1.00e+6 Hz |
0.0153 @Frequency 1.00e+6 Hz |
ASTM D 150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |