SABIC Innovative Plastics Geloy XTPM309 ASA+PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ASA Polymer , Polycarbonate (PC) , Polycarbonate/ASA Alloy, Unreinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | GELOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Geloy XTPM309 ASA+PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
XTPM309 is a modified HRA170 with improved processing stability.Typical properties measured on natural material.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.60 % @Temperature 23.0 °C |
0.60 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 4.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
4.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| 5.0 g/10 min @Load 5.00 kg, Temperature 240 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 464 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 | |
| 13 g/10 min @Load 5.00 kg, Temperature 260 °C |
13 g/10 min @Load 11.0 lb, Temperature 500 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 |
| 62.0 MPa | 8990 psi | 5 mm/min; ISO 527 | |
| 65.0 MPa | 9430 psi | Type I, 5 mm/min; ASTM D 638 | |
| 68.0 MPa | 9860 psi | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D 638 | |
| 59.0 MPa | 8560 psi | 50 mm/min; ISO 527 | |
| 60.0 MPa | 8700 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | >= 100 % | >= 100 % | Type I, 50 mm/min; ASTM D 638 |
| >= 100 % | >= 100 % | Type I, 5 mm/min; ASTM D 638 | |
| >= 100 % | >= 100 % | 5 mm/min; ISO 527 | |
| >= 100 % | >= 100 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % | 5.0 % | 5 mm/min; ISO 527 |
| 5.0 % | 5.0 % | 50 mm/min; ISO 527 | |
| 5.2 % | 5.2 % | Type I, 5 mm/min; ASTM D 638 | |
| 5.3 % | 5.3 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 2.33 GPa | 338 ksi | 5 mm/min; ASTM D 638 |
| 2.35 GPa | 341 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 85.0 MPa | 12300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.25 GPa | 326 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched | 0.850 J/cm @Temperature -30.0 °C |
1.59 ft-lb/in @Temperature -22.0 °F |
ASTM D 256 |
| 3.45 J/cm @Temperature -20.0 °C |
6.46 ft-lb/in @Temperature -4.00 °F |
ASTM D 256 | |
| 5.45 J/cm @Temperature -10.0 °C |
10.2 ft-lb/in @Temperature 14.0 °F |
ASTM D 256 | |
| 6.35 J/cm @Temperature 0.000 °C |
11.9 ft-lb/in @Temperature 32.0 °F |
ASTM D 256 | |
| 6.85 J/cm @Temperature 23.0 °C |
12.8 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 | |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A |
| 18.0 kJ/m² @Temperature -20.0 °C |
8.57 ft-lb/in² @Temperature -4.00 °F |
80*10*4; ISO 180/1A | |
| 28.0 kJ/m² @Temperature -10.0 °C |
13.3 ft-lb/in² @Temperature 14.0 °F |
80*10*4; ISO 180/1A | |
| 47.0 kJ/m² @Temperature 0.000 °C |
22.4 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| 55.0 kJ/m² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 2.40 J/cm² @Temperature -30.0 °C |
11.4 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 6.10 J/cm² @Temperature 23.0 °C |
29.0 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
44.4 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Hot Ball Pressure Test | <= 129 °C | <= 264 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 264 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 109 °C | 228 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 128 °C | 262 °F | Rate B/50; ISO 306 |
| 130 °C | 266 °F | Rate B/120; ISO 306 | |
| 141 °C | 286 °F | Rate A/50; ISO 306 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 6.20e+15 ohm-cm | 6.20e+15 ohm-cm | ASTM D 257 |
| Surface Resistance | 2.40e+16 ohm | 2.40e+16 ohm | ASTM D 257 |
| Dielectric Strength | 27.1 kV/mm @Thickness 1.60 mm |
688 kV/in @Thickness 0.0630 in |
in oil; ASTM D 149 |
| Dissipation Factor | 0.0126 @Frequency 1.00e+6 Hz |
0.0126 @Frequency 1.00e+6 Hz |
ASTM D 150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 |