SABIC Innovative Plastics Geloy XTWM206 ASA (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name GELOY
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Geloy XTWM206 ASA (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Next generation ASA optimized for outstanding weatherability, colorability and higher heat applications requiring UV exposure resistance.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D 792
Density 1.09 g/cc
0.0394 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.20 %
0.20 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.50 %

@Temperature 23.0 °C
0.50 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
on tensile bar; SABIC Method
0.0040 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0075 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0075 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 7.1 g/10 min

@Load 5.00 kg,
Temperature 260 °C
7.1 g/10 min

@Load 11.0 lb,
Temperature 500 °F
ASTM D 1238
7.2 g/10 min

@Load 3.80 kg,
Temperature 280 °C
7.2 g/10 min

@Load 8.38 lb,
Temperature 536 °F
ASTM D 1238
8.8 g/10 min

@Load 10.0 kg,
Temperature 220 °C
8.8 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D 1238
9.0 g/10 min

@Load 5.00 kg,
Temperature 260 °C
9.0 g/10 min

@Load 11.0 lb,
Temperature 500 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 100
100
ASTM D 785
Tensile Strength at Break 36.0 MPa
5220 psi
Type I, 5 mm/min; ASTM D 638
36.0 MPa
5220 psi
50 mm/min; ISO 527
37.0 MPa
5370 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 43.0 MPa
6240 psi
Type I, 5 mm/min; ASTM D 638
45.0 MPa
6530 psi
50 mm/min; ISO 527
46.0 MPa
6670 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 26 %
26 %
Type I, 50 mm/min; ASTM D 638
27 %
27 %
Type I, 5 mm/min; ASTM D 638
36 %
36 %
50 mm/min; ISO 527
Elongation at Yield 2.5 %
2.5 %
Type I, 5 mm/min; ASTM D 638
2.7 %
2.7 %
Type I, 50 mm/min; ASTM D 638
2.8 %
2.8 %
50 mm/min; ISO 527
Tensile Modulus 2.35 GPa
341 ksi
1 mm/min; ISO 527
2.36 GPa
342 ksi
5 mm/min; ASTM D 638
2.40 GPa
348 ksi
50 mm/min; ASTM D 638
Flexural Yield Strength 64.0 MPa
9280 psi
2 mm/min; ISO 178
74.0 MPa
10700 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.38 GPa
345 ksi
2 mm/min; ISO 178
2.45 GPa
355 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.350 J/cm

@Temperature -30.0 °C
0.656 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
2.10 J/cm

@Temperature 23.0 °C
3.93 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 3.00 kJ/m²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
15.0 kJ/m²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.10 J/cm²

@Temperature 23.0 °C
5.23 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 3.00 J

@Temperature -30.0 °C
2.21 ft-lb

@Temperature -22.0 °F
Instrumented Impact Total Energy; ASTM D 3763
36.0 J

@Temperature 23.0 °C
26.6 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 83.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
84.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 94.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
94.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 98.0 °C
208 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
97.0 °C

@Thickness 3.20 mm
207 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 84.0 °C
183 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
84.0 °C

@Thickness 3.20 mm
183 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 95.0 °C
203 °F
Rate B/50; ISO 306
98.0 °C
208 °F
Rate B/50; ASTM D 1525
99.0 °C
210 °F
Rate B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94
Optical Properties Metric English Comments
Gloss 93 %
93 %
untextured, 60 degrees; ASTM D 523
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C Pass85
IEC 60695-10-2
UV-light, water exposure/immersion F1
UL 746C