SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Konduit |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP KONDUIT* PTF2BXXX is a compound based on Nylon 6 resin containing Glass Fiber, Proprietary Thermal Filler. Added features of this material include: Thermally Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Moisture Absorption | 0.400 % | 0.400 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0072 cm/cm @Time 86400 sec |
0.0072 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0118 cm/cm @Time 86400 sec |
0.0118 in/in @Time 24.0 hour |
ISO 294 |
| 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 81.0 MPa | 11700 psi | ISO 527 |
| 88.0 MPa | 12800 psi | ASTM D638 | |
| Elongation at Break | 2.4 % | 2.4 % | ASTM D638 |
| 2.8 % | 2.8 % | ISO 527 | |
| Tensile Modulus | 10.16 GPa | 1474 ksi | 1 mm/min; ISO 527 |
| 10.75 GPa | 1559 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 151 MPa | 21900 psi | ISO 178 |
| 168 MPa | 24400 psi | ASTM D790 | |
| Flexural Modulus | 9.65 GPa | 1400 ksi | ISO 178 |
| 10.61 GPa | 1539 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.44 J/cm | 2.70 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.48 | 0.48 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.39 | 0.39 | ASTM D3702 Modified |
| K (wear) Factor | 2163 x 10-8 mm³/N-M | 1074 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.10 W/m-K | 7.63 BTU-in/hr-ft²-°F | ASTM E 1530 |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 174 °C @Thickness 3.20 mm |
345 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Ovation Polymers Nemcon™ E PK DP104 Polyetheretherketone, Carbon Fiber Reinforced
- Momentive Performance Materials AC6111 Boron Nitride (BN) Powder
- KaMin Omnifil® Kaolin Clay - Filler
- Multibase Multi-ABS 802 Utility Grade White
- Eagle Brass 260 Cartridge Brass, Spring
- Cytec EN-13 (Conap) Casting, Potting, and Molding Compound
- Arkema Group Rilsan® AMN Y TLD Nylon 12, MoS2 Filled (Conditioned)
- Arlon 55986C028 0.0295" Cured/Uncured Silicone Rubber with Fiberglass Substrate
- Arlon R35232B050 0.050" Fully Cured, Static Dissipating Silicone Rubber
Copyright © lookpolymers.com All Rights Reserved