SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP AL003 ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing 15% PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ASTM D792
1.13 g/cc
0.0408 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
0.310 %
0.310 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm

@Time 86400 sec
0.0080 - 0.010 in/in

@Time 24.0 hour
ASTM D955
0.0080 - 0.010 cm/cm

@Time 86400 sec
0.0080 - 0.010 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 32.0 MPa
4640 psi
ASTM D638
32.0 MPa
4640 psi
ISO 527
Tensile Strength, Yield 35.0 MPa
5080 psi
ASTM D638
35.0 MPa
5080 psi
ISO 527
Elongation at Break 11.6 %
11.6 %
ISO 527
14.7 %
14.7 %
ASTM D638
Elongation at Yield 2.3 %
2.3 %
ASTM D638
2.7 %
2.7 %
ISO 527
Tensile Modulus 2.28 GPa
331 ksi
1 mm/min; ISO 527
2.41 GPa
350 ksi
50 mm/min; ASTM D638
Flexural Strength 61.0 MPa
8850 psi
ISO 178
62.0 MPa
8990 psi
ASTM D790
Flexural Modulus 2.00 GPa
290 ksi
ISO 178
2.06 GPa
299 ksi
ASTM D790
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.02 J/cm
3.78 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 21.0 kJ/m²
9.99 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 11.0 J
8.11 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 8.00 J
5.90 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.22
0.22
ASTM D3702 Modified
Coefficient of Friction, Static 0.11
0.11
ASTM D3702 Modified
K (wear) Factor 201 x 10-8 mm³/N-M
100 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 95.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
53.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
95.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
53.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 93.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
95.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
52.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 81.0 °C
178 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
77.0 °C

@Thickness 3.20 mm
171 °F

@Thickness 0.126 in
unannealed; ASTM D648