SABIC Innovative Plastics LNP LUBRICOMP DAL22 PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DAL22 PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DAL22 is a compound based on Polycarbonate resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.27 g/cc
0.0459 lb/in³
ASTM D792
1.27 g/cc
0.0459 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0060 cm/cm

@Time 86400 sec
0.0060 in/in

@Time 24.0 hour
ASTM D955
0.0060 cm/cm

@Time 86400 sec
0.0060 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0070 cm/cm

@Time 86400 sec
0.0070 in/in

@Time 24.0 hour
ASTM D955
0.0071 cm/cm

@Time 86400 sec
0.0071 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
ASTM D638
57.0 MPa
8270 psi
ISO 527
Tensile Strength, Yield 59.0 MPa
8560 psi
ASTM D638
59.0 MPa
8560 psi
ISO 527
Elongation at Break 8.0 %
8.0 %
ISO 527
8.8 %
8.8 %
ASTM D638
Elongation at Yield 5.2 %
5.2 %
ISO 527
5.3 %
5.3 %
ASTM D638
Tensile Modulus 2.75 GPa
399 ksi
50 mm/min; ASTM D638
2.82 GPa
409 ksi
1 mm/min; ISO 527
Flexural Strength 84.0 MPa
12200 psi
ISO 178
Flexural Modulus 2.75 GPa
399 ksi
ASTM D790
3.00 GPa
435 ksi
ISO 178
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.20 J/cm
13.5 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 41.0 kJ/m²
19.5 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 10.0 J
7.38 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.28
0.28
ASTM D3702 Modified
Coefficient of Friction, Static 0.18
0.18
ASTM D3702 Modified
K (wear) Factor 42.3 x 10-8 mm³/N-M
21.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 69.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
70.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 55.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
55.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 138 °C
280 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
137 °C

@Thickness 3.20 mm
279 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
127 °C

@Thickness 3.20 mm
261 °F

@Thickness 0.126 in
unannealed; ASTM D648