SABIC Innovative Plastics LNP LUBRICOMP DFL32P PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP DFL32P PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* DFL32P is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated, Exceptional Processing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792 |
| 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.120 % | 0.120 % | 50% RH, 24 hrs; ASTM D570 |
| 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Time 86400 sec |
0.0050 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D638 |
| 75.0 MPa | 10900 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 76.0 MPa | 11000 psi | Type I, 5 mm/min; ASTM D638 |
| 77.0 MPa | 11200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.3 % | 3.3 % | Type I, 5 mm/min; ASTM D638 |
| 3.4 % | 3.4 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 |
| 2.9 % | 2.9 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 4.51 GPa | 654 ksi | 1 mm/min; ISO 527 |
| 4.78 GPa | 693 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 123 MPa | 17800 psi | ISO 178 |
| 128 MPa | 18600 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 128 MPa | 18600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 4.24 GPa | 615 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.32 GPa | 627 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.05 J/cm | 11.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² | 5.23 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 21.0 J @Temperature 23.0 °C |
15.5 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.42 | 0.42 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 30.2 x 10-8 mm³/N-M | 15.0 x 10-10 in³-min/ft-lb-hr | Ring; ASTM D3702 Modified |
| 280 x 10-8 mm³/N-M | 139 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 35.1 µm/m-°C @Temperature -30.0 - 30.0 °C |
19.5 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 74.6 µm/m-°C @Temperature -30.0 - 30.0 °C |
41.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 139 °C | 282 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 140 °C @Thickness 3.20 mm |
284 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 134 °C | 273 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 135 °C @Thickness 3.20 mm |
275 °F @Thickness 0.126 in |
unannealed; ASTM D648 |