SABIC Innovative Plastics LNP LUBRICOMP DFL34 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DFL34 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* DFL34 is a compound based on Polycarbonate resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Specific Gravity 1.46 g/cc
1.46 g/cc
ASTM D792
Density 1.46 g/cc
0.0527 lb/in³
ASTM D792
1.46 g/cc
0.0527 lb/in³
ISO 1183
Moisture Absorption 0.110 %
0.110 %
50% RH, 24 hrs; ASTM D570
0.160 %
0.160 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Time 86400 sec
 0.0020 - 0.0040 in/in

@Time 24.0 hour
 ASTM D955
0.0020 - 0.0040 cm/cm

@Time 86400 sec
 0.0020 - 0.0040 in/in

@Time 24.0 hour
 ISO 294
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Time 86400 sec
 0.0030 - 0.0050 in/in

@Time 24.0 hour
 ISO 294
0.0030 - 0.0060 cm/cm

@Time 86400 sec
 0.0030 - 0.0060 in/in

@Time 24.0 hour
 ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 89.0 MPa
12900 psi
5 mm/min; ISO 527
95.0 MPa
13800 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 94.0 MPa
13600 psi
50 mm/min; ISO 527
97.0 MPa
14100 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 3.3 %
3.3 %
Type I, 5 mm/min; ASTM D638
3.5 %
3.5 %
5 mm/min; ISO 527
Elongation at Yield 2.8 %
2.8 %
Type I, 5 mm/min; ASTM D638
2.9 %
2.9 %
5 mm/min; ISO 527
Tensile Modulus 6.50 GPa
943 ksi
1 mm/min; ISO 527
6.86 GPa
995 ksi
50 mm/min; ASTM D638
Flexural Strength 143 MPa
20700 psi
ASTM D790
153 MPa
22200 psi
ISO 178
Flexural Yield Strength 144 MPa
20900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 4.91 GPa
712 ksi
1.3 mm/min, 50 mm span; ASTM D790
6.01 GPa
872 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.69 J/cm
3.17 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.80 J/cm
14.6 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 47.0 kJ/m²
22.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 22.0 J
16.2 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 7.00 J
5.16 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.52
0.52
ASTM D3702 Modified
Coefficient of Friction, Static 0.67
0.67
ASTM D3702 Modified
K (wear) Factor 153 x 10-8 mm³/N-M
76.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 28.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 15.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
28.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 15.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 66.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 36.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
66.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 36.7 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 147 °C
297 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
147 °C

@Thickness 3.20 mm
 297 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 144 °C
291 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
143 °C

@Thickness 3.20 mm
 289 °F

@Thickness 0.126 in
 unannealed; ASTM D648