SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP DFL369XF PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* DFL369XF is a compound based on Polycarbonate resin containing Glass Fiber, PTFE, Flame Retardant. Added features of this material include: Internally Lubricated, Flame Retardant.
Physical Properties Metric English Comments
Density 1.60 g/cc
0.0578 lb/in³
ASTM D792
1.60 g/cc
0.0578 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Time 86400 sec
0.0010 - 0.0030 in/in

@Time 24.0 hour
ASTM D955
0.0021 cm/cm

@Time 86400 sec
0.0021 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0030 - 0.0050 cm/cm

@Time 86400 sec
0.0030 - 0.0050 in/in

@Time 24.0 hour
ASTM D955
0.0040 cm/cm

@Time 86400 sec
0.0040 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 112 MPa
16200 psi
ASTM D638
115 MPa
16700 psi
ISO 527
Tensile Strength, Yield 115 MPa
16700 psi
ISO 527
116 MPa
16800 psi
ASTM D638
Elongation at Break 2.1 %
2.1 %
ISO 527
2.3 %
2.3 %
ASTM D638
Elongation at Yield 2.1 %
2.1 %
ISO 527
2.2 %
2.2 %
ASTM D638
Tensile Modulus 9.93 GPa
1440 ksi
1 mm/min; ISO 527
10.34 GPa
1500 ksi
50 mm/min; ASTM D638
Flexural Strength 173 MPa
25100 psi
ISO 178
179 MPa
26000 psi
ASTM D790
Flexural Modulus 8.96 GPa
1300 ksi
ASTM D790
9.20 GPa
1330 ksi
ISO 178
Izod Impact, Notched 6.62 J/cm
12.4 ft-lb/in
ASTM D256
Izod Impact, Unnotched 1.22 J/cm
2.29 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 11.0 kJ/m²
5.23 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 39.0 kJ/m²
18.6 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 19.0 J
14.0 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 4.00 J
2.95 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.51
0.51
ASTM D3702 Modified
Coefficient of Friction, Static 0.52
0.52
ASTM D3702 Modified
K (wear) Factor 56.4 x 10-8 mm³/N-M
28.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 54.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
54.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
30.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 21.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
12.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
22.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
12.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
138 °C

@Thickness 3.20 mm
280 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 135 °C
275 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
135 °C

@Thickness 3.20 mm
275 °F

@Thickness 0.126 in
unannealed; ASTM D648