Material Notes:
LNP LUBRICOMP* DP003EH is a compound based on Polycarbonate resin containing 15% PTFE/Silicone. Added features of this material include: Easy Molding, Internally Lubricated, Healthcare.
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D792
Density 1.26 g/cc
0.0455 lb/in³
ASTM D792
Moisture Absorption 0.130 %
0.130 %
50% RH, 24 hrs; ASTM D570
0.190 %
0.190 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0090 cm/cm

@Time 86400 sec
0.0060 - 0.0090 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 - 0.010 cm/cm

@Time 86400 sec
0.0070 - 0.010 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 43.0 MPa
6240 psi
Type I, 5 mm/min; ASTM D638
46.0 MPa
6670 psi
5 mm/min; ISO 527
46.0 MPa
6670 psi
ASTM D638
Tensile Strength, Yield 40.0 MPa
5800 psi
ASTM D638
48.0 MPa
6960 psi
5 mm/min; ISO 527
49.0 MPa
7110 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 17 %
17 %
ASTM D638
49 %
49 %
Type I, 5 mm/min; ASTM D638
116 %
116 %
5 mm/min; ISO 527
Elongation at Yield 5.0 %
5.0 %
ASTM D638
5.7 %
5.7 %
5 mm/min; ISO 527
5.9 %
5.9 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.01 GPa
292 ksi
1 mm/min; ISO 527
2.03 GPa
294 ksi
50 mm/min; ASTM D638
Flexural Strength 61.0 MPa
8850 psi
ISO 178
77.0 MPa
11200 psi
ASTM D790
Flexural Modulus 1.92 GPa
278 ksi
2 mm/min; ISO 178
2.06 GPa
299 ksi
ASTM D790
2.10 GPa
305 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 4.74 J/cm
8.88 ft-lb/in
ASTM D256
Izod Impact, Unnotched 15.1 J/cm
28.3 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 41.0 kJ/m²
19.5 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 174 kJ/m²
82.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 29.0 J

@Temperature 23.0 °C
21.4 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 20.0 J
14.8 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.29
0.29
ASTM D3702 Modified
Coefficient of Friction, Static 0.15
0.15
ASTM D3702 Modified
K (wear) Factor 56.4 x 10-8 mm³/N-M
28.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 78.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
43.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 76.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
42.2 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 140 °C
284 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
141 °C

@Thickness 3.20 mm
286 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
261 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
128 °C

@Thickness 3.20 mm
262 °F

@Thickness 0.126 in
unannealed; ASTM D648