SABIC Innovative Plastics LNP LUBRICOMP EFL34HL PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP EFL34HL PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* EFL34HL is a compound based on Polyetherimide resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractable.
Physical Properties Metric English Comments
Density 1.54 g/cc
0.0556 lb/in³
ASTM D792
1.54 g/cc
0.0556 lb/in³
ISO 1183
Moisture Absorption 0.170 %
0.170 %
50% RH, 24 hrs; ASTM D570
0.230 %
0.230 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Time 86400 sec
0.0030 in/in

@Time 24.0 hour
ASTM D955
0.0033 cm/cm

@Time 86400 sec
0.0033 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0060 cm/cm

@Time 86400 sec
0.0060 in/in

@Time 24.0 hour
ASTM D955
0.0060 cm/cm

@Time 86400 sec
0.0060 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 113 MPa
16400 psi
ASTM D638
113 MPa
16400 psi
ISO 527
Elongation at Break 2.2 %
2.2 %
ASTM D638
2.2 %
2.2 %
ISO 527
Tensile Modulus 7.40 GPa
1070 ksi
1 mm/min; ISO 527
7.58 GPa
1100 ksi
50 mm/min; ASTM D638
Flexural Strength 179 MPa
26000 psi
ASTM D790
181 MPa
26300 psi
ISO 178
Flexural Modulus 7.51 GPa
1090 ksi
ASTM D790
7.94 GPa
1150 ksi
ISO 178
Izod Impact, Notched 0.690 J/cm
1.29 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.80 J/cm
8.99 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 20.0 kJ/m²
9.52 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 32.0 kJ/m²
15.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J
5.90 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 204 °C
399 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
203 °C

@Thickness 3.20 mm
397 °F

@Thickness 0.126 in
unannealed; ASTM D648