SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU

Category Polymer , Thermoplastic , Polysulfone (PSU)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP GFL36L PSU.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* GFL36L is a compound based on Polysulfone resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Internally Lubricated, Low Extractible.
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
ASTM D792
1.62 g/cc
0.0585 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0026 cm/cm

@Time 86400 sec
0.0026 in/in

@Time 24.0 hour
ISO 294
0.0020 - 0.0040 cm/cm

@Time 86400 sec
0.0020 - 0.0040 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D955
0.0051 cm/cm

@Time 86400 sec
0.0051 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 87.0 MPa
12600 psi
ISO 527
88.0 MPa
12800 psi
ASTM D638
Tensile Strength, Yield 87.0 MPa
12600 psi
ISO 527
88.0 MPa
12800 psi
ASTM D638
Elongation at Break 1.2 %
1.2 %
ISO 527
1.3 %
1.3 %
ASTM D638
Elongation at Yield 1.3 %
1.3 %
ASTM D638
1.3 %
1.3 %
ISO 527
Tensile Modulus 9.33 GPa
1350 ksi
1 mm/min; ISO 527
10.34 GPa
1500 ksi
50 mm/min; ASTM D638
Flexural Strength 110 MPa
16000 psi
ASTM D790
121 MPa
17500 psi
ISO 178
Flexural Modulus 8.96 GPa
1300 ksi
ASTM D790
9.00 GPa
1310 ksi
ISO 178
Izod Impact, Notched 0.740 J/cm
1.39 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.41 J/cm
6.39 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 23.0 kJ/m²
10.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 14.0 J
10.3 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.42
0.42
ASTM D3702 Modified
Coefficient of Friction, Static 0.62
0.62
ASTM D3702 Modified
K (wear) Factor 88.6 x 10-8 mm³/N-M
44.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
30.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
17.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 24.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
13.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
25.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
14.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 186 °C
367 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
185 °C

@Thickness 3.20 mm
365 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 181 °C
358 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
180 °C

@Thickness 3.20 mm
356 °F

@Thickness 0.126 in
unannealed; ASTM D648