SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP KP002 Acetal Copoly (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* KP002 is a compound based on Acetal Copolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ASTM D792
1.43 g/cc
0.0517 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.022 cm/cm

@Time 86400 sec
0.022 in/in

@Time 24.0 hour
ASTM D955
0.022 cm/cm

@Time 86400 sec
0.022 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.022 cm/cm

@Time 86400 sec
0.022 in/in

@Time 24.0 hour
ASTM D955
0.022 cm/cm

@Time 86400 sec
0.022 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
ASTM D638
48.0 MPa
6960 psi
Type I, 5 mm/min; ASTM D638
48.0 MPa
6960 psi
5 mm/min; ISO 527
Tensile Strength, Yield 46.0 MPa
6670 psi
ASTM D638
46.0 MPa
6670 psi
ISO 527
49.0 MPa
7110 psi
5 mm/min; ISO 527
49.0 MPa
7110 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 7.0 %
7.0 %
Flexural Strain, break, 2 mm/min; ISO 178
28.4 %
28.4 %
5 mm/min; ISO 527
28.6 %
28.6 %
Type I, 5 mm/min; ASTM D638
40.9 %
40.9 %
ASTM D638
Elongation at Yield 17.9 %
17.9 %
5 mm/min; ISO 527
18.3 %
18.3 %
Type I, 5 mm/min; ASTM D638
26.3 %
26.3 %
ASTM D638
29 %
29 %
ISO 527
Tensile Modulus 2.33 GPa
338 ksi
1 mm/min; ISO 527
2.75 GPa
399 ksi
50 mm/min; ASTM D638
Flexural Strength 61.0 MPa
8850 psi
ISO 178
Flexural Yield Strength 69.0 MPa
10000 psi
2 mm/min; ISO 178
Flexural Modulus 1.91 GPa
277 ksi
1.3 mm/min, 50 mm span; ASTM D790
1.99 GPa
289 ksi
2 mm/min; ISO 178
2.00 GPa
290 ksi
ISO 178
2.06 GPa
299 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 10.68 J/cm
20.01 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 74.0 kJ/m²
35.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 5.00 J
3.69 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.31
0.31
ASTM D3702 Modified
Coefficient of Friction, Static 0.18
0.18
ASTM D3702 Modified
K (wear) Factor 16.1 x 10-8 mm³/N-M
8.00 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 106 µm/m-°C

@Temperature -40.0 - 40.0 °C
58.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
106 µm/m-°C

@Temperature -40.0 - 40.0 °C
58.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 103 µm/m-°C

@Temperature -40.0 - 40.0 °C
57.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
103 µm/m-°C

@Temperature -40.0 - 40.0 °C
57.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 146 °C
295 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
156 °C

@Thickness 3.20 mm
313 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
92.0 °C

@Thickness 3.20 mm
198 °F

@Thickness 0.126 in
unannealed; ASTM D648