SABIC Innovative Plastics LNP LUBRICOMP KP003AXZ Acetal Homopoly (Asia Pacific)

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP KP003AXZ Acetal Homopoly (Asia Pacific).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* KP003AXZ is a compound based on Acetal Homopolymer resin containing PTFE, Silicone. Added features of this material include: Internally Lubricated.

Physical Properties	Metric	English	Comments
Density	1.47 g/cc	0.0531 lb/inÂ³	ASTM D792
	1.47 g/cc	0.0531 lb/inÂ³	ISO 1183
Moisture Absorption	0.300 %	0.300 %	50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.024 cm/cm @Time 86400 sec	0.024 in/in @Time 24.0 hour	ASTM D955
	0.024 cm/cm @Time 86400 sec	0.024 in/in @Time 24.0 hour	ISO 294
Linear Mold Shrinkage, Transverse	0.025 cm/cm @Time 86400 sec	0.025 in/in @Time 24.0 hour	ASTM D955
	0.025 cm/cm @Time 86400 sec	0.025 in/in @Time 24.0 hour	ISO 294

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	52.0 MPa	7540 psi	ASTM D638
	53.0 MPa	7690 psi	ISO 527
Tensile Strength, Yield	53.0 MPa	7690 psi	ASTM D638
	53.0 MPa	7690 psi	ISO 527
Elongation at Break	15.1 %	15.1 %	ISO 527
	28.8 %	28.8 %	ASTM D638
Elongation at Yield	15 %	15 %	ISO 527
	20.9 %	20.9 %	ASTM D638
Tensile Modulus	2.57 GPa	373 ksi	1 mm/min; ISO 527
	2.75 GPa	399 ksi	50 mm/min; ASTM D638
Flexural Strength	65.0 MPa	9430 psi	ISO 178
Flexural Modulus	2.75 GPa	399 ksi	ASTM D790
	3.00 GPa	435 ksi	ISO 178
Izod Impact, Notched	0.530 J/cm	0.993 ft-lb/in	ASTM D256
Izod Impact, Unnotched	10.14 J/cm	19.00 ft-lb/in	ASTM D4812
Izod Impact, Notched (ISO)	5.00 kJ/mÂ²	2.38 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	53.0 kJ/mÂ²	25.2 ft-lb/inÂ²	80104; ISO 180/1U
Dart Drop, Total Energy	1.00 J	0.738 ft-lb	Instrumented Impact Energy @ peak; ASTM D3763
Impact Test	1.00 J	0.738 ft-lb	Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic	0.21	0.21	ASTM D3702 Modified
Coefficient of Friction, Static	0.11	0.11	ASTM D3702 Modified
K (wear) Factor	22.2 x 10^-8 mmÂ³/N-M	11.0 x 10^-10 inÂ³-min/ft-lb-hr	Washer; ASTM D3702 Modified

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	95.4 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	53.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	96.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	53.3 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	95.4 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	53.0 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ASTM E 831
	96.0 Âµm/m-Â°C @Temperature -40.0 - 40.0 Â°C	53.3 Âµin/in-Â°F @Temperature -40.0 - 104 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	157 Â°C	315 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
	162 Â°C @Thickness 3.20 mm	324 Â°F @Thickness 0.126 in	unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	88.0 Â°C	190 Â°F	Flatw 80104 sp=64mm; ISO 75/Af
	92.0 Â°C @Thickness 3.20 mm	198 Â°F @Thickness 0.126 in	unannealed; ASTM D648

Users viewing this material also viewed the following: