SABIC Innovative Plastics LNP LUBRICOMP OCL36 PPS - Linear

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP OCL36 PPS - Linear.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* OCL36 is a compound based on PPS - Linear resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ASTM D792
1.52 g/cc
0.0549 lb/in³
ISO 1183
Moisture Absorption 0.0300 %
0.0300 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.00040 - 0.0010 cm/cm

@Time 86400 sec
0.00040 - 0.0010 in/in

@Time 24.0 hour
ASTM D955
0.00040 - 0.0010 cm/cm

@Time 86400 sec
0.00040 - 0.0010 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0030 - 0.0040 cm/cm

@Time 86400 sec
0.0030 - 0.0040 in/in

@Time 24.0 hour
ASTM D955
0.0036 - 0.0040 cm/cm

@Time 86400 sec
0.0036 - 0.0040 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 167 MPa
24200 psi
ISO 527
168 MPa
24400 psi
ASTM D638
Elongation at Break 1.1 %
1.1 %
ISO 527
1.4 %
1.4 %
ASTM D638
Tensile Modulus 21.51 GPa
3120 ksi
50 mm/min; ASTM D638
30.68 GPa
4450 ksi
1 mm/min; ISO 527
Flexural Strength 259 MPa
37600 psi
ASTM D790
262 MPa
38000 psi
ISO 178
Flexural Modulus 21.11 GPa
3062 ksi
ASTM D790
21.11 GPa
3062 ksi
ISO 178
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.43 J/cm
8.30 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 31.0 kJ/m²
14.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 15.0 J
11.1 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.39
0.39
ASTM D3702 Modified
Coefficient of Friction, Static 0.34
0.34
ASTM D3702 Modified
K (wear) Factor 38.3 x 10-8 mm³/N-M
19.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 16.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
9.00 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
17.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
9.78 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 34.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
19.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
34.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
19.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 263 °C
505 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
267 °C

@Thickness 3.20 mm
513 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.80 mm
V-0

@Thickness 0.0709 in
UL 94 by SABIC-IP