SABIC Innovative Plastics LNP LUBRICOMP OCP36A PPS - Branched

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP OCP36A PPS - Branched.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* OCP36A is a compound based on PPS - Branched resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this material include: Wear Resistant, Electrically Conductive.
Physical Properties Metric English Comments
Density 1.49 g/cc
0.0538 lb/in³
ASTM D792
1.53 g/cc
0.0553 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0015 cm/cm

@Time 86400 sec
0.0015 in/in

@Time 24.0 hour
ISO 294
0.0020 cm/cm

@Time 86400 sec
0.0020 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0066 cm/cm

@Time 86400 sec
0.0066 in/in

@Time 24.0 hour
ISO 294
0.0070 cm/cm

@Time 86400 sec
0.0070 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 113 MPa
16400 psi
ISO 527
119 MPa
17300 psi
ASTM D638
Tensile Strength, Yield 113 MPa
16400 psi
ISO 527
127 MPa
18400 psi
ASTM D638
Elongation at Break 0.70 %
0.70 %
ISO 527
1.6 %
1.6 %
ASTM D638
Elongation at Yield 0.70 %
0.70 %
ISO 527
0.90 %
0.90 %
ASTM D638
Tensile Modulus 18.61 GPa
2699 ksi
50 mm/min; ASTM D638
19.88 GPa
2883 ksi
1 mm/min; ISO 527
Flexural Strength 176 MPa
25500 psi
ISO 178
229 MPa
33200 psi
ASTM D790
Flexural Modulus 19.0 GPa
2760 ksi
ISO 178
20.13 GPa
2920 ksi
ASTM D790
Izod Impact, Notched 0.370 J/cm
0.693 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.20 J/cm
5.99 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J
4.43 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.36
0.36
ASTM D3702 Modified
Coefficient of Friction, Static 0.30
0.30
ASTM D3702 Modified
K (wear) Factor 30.2 x 10-8 mm³/N-M
15.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 36.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
20.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
36.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
20.0 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature -40.0 - 40.0 °C
3.89 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
7.20 µm/m-°C

@Temperature -40.0 - 40.0 °C
4.00 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 272 °C
522 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
273 °C

@Thickness 3.20 mm
523 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 248 °C
478 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
258 °C

@Thickness 3.20 mm
496 °F

@Thickness 0.126 in
unannealed; ASTM D648