- SABIC Innovative Plastics LNP LUBRICOMP OX88533 PPS
SABIC Innovative Plastics LNP LUBRICOMP OX88533 PPS
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP OX88533 PPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* OX88533 is a compound based on Polyphenylene Sulfide resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.69 g/cc | 0.0611 lb/in³ | ASTM D792 |
| 1.69 g/cc | 0.0611 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00090 cm/cm @Time 86400 sec |
0.00090 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0053 cm/cm @Time 86400 sec |
0.0053 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 144 MPa | 20900 psi | ASTM D638 |
| 146 MPa | 21200 psi | ISO 527 | |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| 1.8 % | 1.8 % | ISO 527 | |
| Tensile Modulus | 12.18 GPa | 1767 ksi | 1 mm/min; ISO 527 |
| 13.1 GPa | 1900 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| 208 MPa | 30200 psi | ISO 178 | |
| Flexural Modulus | 10.96 GPa | 1590 ksi | ASTM D790 |
| 11.44 GPa | 1659 ksi | ISO 178 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.28 J/cm | 9.89 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 38.0 kJ/m² | 18.1 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J | 5.16 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.43 | 0.43 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.34 | 0.34 | ASTM D3702 Modified |
| K (wear) Factor | 119 x 10-8 mm³/N-M | 59.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 263 °C @Thickness 3.20 mm |
505 °F @Thickness 0.126 in |
unannealed; ASTM D648 |