- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyethylene (PE)
- SABIC Innovative Plastics LNP LUBRICOMP PDXF89080 PE
SABIC Innovative Plastics LNP LUBRICOMP PDXF89080 PE
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP PDXF89080 PE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* LUBRICOMP* PDXF89080 is a compound based on Polyethylene containing Proprietary Fillers. Added feature of this grade is: Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.920 g/cc | 0.920 g/cc | ASTM D792 |
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0300 % | 0.0300 % | 50% RH, 24 hrs; ASTM D570 |
| 0.0300 % | 0.0300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 8.00 MPa | 1160 psi | 5 mm/min; ISO 527 |
| 9.00 MPa | 1310 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | 5 mm/min; ISO 527 |
| 10.0 MPa | 1450 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 90 % | 90 % | Type I, 5 mm/min; ASTM D638 |
| 164 % | 164 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 73 % | 73 % | Type I, 5 mm/min; ASTM D638 |
| 88 % | 88 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 0.200 GPa | 29.0 ksi | 5 mm/min; ASTM D638 |
| 0.240 GPa | 34.8 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 5.00 MPa | 725 psi | ISO 178 |
| Flexural Modulus | 0.120 GPa | 17.4 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 0.120 GPa | 17.4 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 3.04 J/cm | 5.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D4812 |
| Izod Impact, Notched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 19.0 J @Temperature 23.0 °C |
14.0 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 19.0 J | 14.0 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 208 µm/m-°C @Temperature -30.0 - 30.0 °C |
116 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 199 µm/m-°C @Temperature -30.0 - 30.0 °C |
111 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 41.0 °C | 106 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 42.0 °C @Thickness 3.20 mm |
108 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 23.0 °C | 73.4 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 23.0 °C @Thickness 3.20 mm |
73.4 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- NYCOA 2366 Plasticized Copolyamide TPE
- Polimeri Europa Dutral® TER 4535 Ethylene - Propylene - Diene Terpolymer
- Lehmann & Voss LUVOCOM® 1105-7442 PEEK, with carbon fiber, easy flowing
- Gwent Electronic Materials C2061027P15 High Brightness Phosphor Ink (Blue)
- Lucas-Milhaupt BRAZE 716 (VTG) Grade 1 Silver Based Cadmium Free Filler Metal
- Solvay Specialty Polymers Ixef® 1022 Polyarylamide (PARA), 50% Glass Fiber (Dry)
- SABIC Innovative Plastics LNP THERMOCOMP AB002 ABS (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP JF004E PES (Asia Pacific)
- DuPont Teijin Films Mylar® HP Polyester Film, 48 Gauge
- Daikin NEOFLON NP-20 FEP Pellets
Copyright © lookpolymers.com All Rights Reserved