SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP RX01514 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* RX01514 is a compound based on Nylon 66 resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.
Physical Properties Metric English Comments
Density 1.14 g/cc
0.0412 lb/in³
ISO 1183
1.15 g/cc
0.0415 lb/in³
ASTM D792
Moisture Absorption 1.10 %
1.10 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.010 - 0.012 cm/cm

@Time 86400 sec
0.010 - 0.012 in/in

@Time 24.0 hour
ASTM D955
0.011 cm/cm

@Time 86400 sec
0.011 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.012 - 0.014 cm/cm

@Time 86400 sec
0.012 - 0.014 in/in

@Time 24.0 hour
ASTM D955
0.013 cm/cm

@Time 86400 sec
0.013 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 71.0 MPa
10300 psi
ASTM D638
78.0 MPa
11300 psi
ISO 527
Tensile Strength, Yield 80.0 MPa
11600 psi
ISO 527
84.0 MPa
12200 psi
ASTM D638
Elongation at Break 19.1 %
19.1 %
ISO 527
21.1 %
21.1 %
ASTM D638
Elongation at Yield 3.9 %
3.9 %
ISO 527
4.2 %
4.2 %
ASTM D638
Tensile Modulus 3.40 GPa
493 ksi
1 mm/min; ISO 527
3.44 GPa
499 ksi
50 mm/min; ASTM D638
Flexural Strength 96.0 MPa
13900 psi
ISO 178
Flexural Modulus 2.75 GPa
399 ksi
ASTM D790
2.80 GPa
406 ksi
ISO 178
Izod Impact, Notched 0.420 J/cm
0.787 ft-lb/in
ASTM D256
Izod Impact, Unnotched 18.95 J/cm
35.50 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 251 kJ/m²
119 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 29.0 J
21.4 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 48.0 J
35.4 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.81
0.81
ASTM D3702 Modified
Coefficient of Friction, Static 0.62
0.62
ASTM D3702 Modified
K (wear) Factor 135 x 10-8 mm³/N-M
67.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 82.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
83.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 86.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
48.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
87.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
48.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 156 °C
313 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
183 °C

@Thickness 3.20 mm
361 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 62.0 °C
144 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
66.0 °C

@Thickness 3.20 mm
151 °F

@Thickness 0.126 in
unannealed; ASTM D648