SABIC Innovative Plastics LNP LUBRICOMP SCL36 PA12

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP SCL36 PA12.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* SCL36 is a compound based on Nylon 12 resin containing 15% PTFE, 30% Carbon Fiber. Added features of this material include: Wear Resistant, Electrically Conductive.
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D792
Density 1.30 g/cc
0.0470 lb/in³
ASTM D792
Moisture Absorption 0.0900 %
0.0900 %
50% RH, 24 hrs; ASTM D570
0.140 %
0.140 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.00040 - 0.00060 cm/cm

@Time 86400 sec
0.00040 - 0.00060 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
5 mm/min; ISO 527
157 MPa
22800 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 1.0 %
1.0 %
5 mm/min; ISO 527
1.9 %
1.9 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 19.42 GPa
2817 ksi
1 mm/min; ISO 527
21.4 GPa
3100 ksi
50 mm/min; ASTM D638
Flexural Strength 206 MPa
29900 psi
ISO 178
214 MPa
31000 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 215 MPa
31200 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 15.8 GPa
2290 ksi
1.3 mm/min, 50 mm span; ASTM D790
16.49 GPa
2392 ksi
2 mm/min; ISO 178
Izod Impact, Notched 1.29 J/cm
2.42 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.86 J/cm
12.9 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 129 kJ/m²
61.4 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 39.0 kJ/m²
18.6 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 14.0 J

@Temperature 23.0 °C
10.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 4.00 J
2.95 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.41
0.41
ASTM D3702 Modified
Coefficient of Friction, Static 0.30
0.30
ASTM D3702 Modified
K (wear) Factor 44.3 x 10-8 mm³/N-M
22.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 29.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
16.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 63.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
35.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 177 °C
351 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
178 °C

@Thickness 3.20 mm
352 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 170 °C
338 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
173 °C

@Thickness 3.20 mm
343 °F

@Thickness 0.126 in
unannealed; ASTM D648