SABIC Innovative Plastics LNP LUBRICOMP UX95672 PPA

Category Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP UX95672 PPA.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* UX95672 is a compound based on Polyphthalamide resin containing Proprietary Filler(s). Added feature of this material is: Wear Resistant.
Physical Properties Metric English Comments
Density 1.46 g/cc
0.0527 lb/in³
ASTM D792
1.46 g/cc
0.0527 lb/in³
ISO 1183
Moisture Absorption 0.280 %
0.280 %
50% RH, 24 hrs; ASTM D570
0.330 %
0.330 %
23°C / 50% RH; ISO 62
Mechanical Properties Metric English Comments
Tensile Strength at Break 132 MPa
19100 psi
ISO 527
163 MPa
23600 psi
ASTM D638
Elongation at Break 1.3 %
1.3 %
ISO 527
1.7 %
1.7 %
ASTM D638
Tensile Modulus 11.48 GPa
1665 ksi
1 mm/min; ISO 527
12.75 GPa
1849 ksi
50 mm/min; ASTM D638
Flexural Strength 255 MPa
37000 psi
ASTM D790
262 MPa
38000 psi
ISO 178
Flexural Modulus 11.23 GPa
1629 ksi
ASTM D790
11.33 GPa
1643 ksi
ISO 178
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.30 J/cm
11.8 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 44.0 kJ/m²
20.9 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 4.00 J
2.95 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 255 °C
491 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
260 °C

@Thickness 3.20 mm
 500 °F

@Thickness 0.126 in
 unannealed; ASTM D648