SABIC Innovative Plastics LNP LUBRICOMP WFL34H PBT

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP WFL34H PBT.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRICOMP* WFL34H is a compound based on PBT resin containing 20% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Healthcare.
Physical Properties Metric English Comments
Specific Gravity 1.59 g/cc
1.59 g/cc
ASTM D792
Density 1.59 g/cc
0.0574 lb/in³
ASTM D792
Moisture Absorption 0.0500 %
0.0500 %
50% RH, 24 hrs; ASTM D570
0.0700 %
0.0700 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Time 86400 sec
0.0040 - 0.0070 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0090 - 0.020 cm/cm

@Time 86400 sec
0.0090 - 0.020 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 121 MPa
17500 psi
50 mm/min; ISO 527
123 MPa
17800 psi
ASTM D638
Tensile Strength, Yield 121 MPa
17500 psi
5 mm/min; ISO 527
123 MPa
17800 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.6 %
2.6 %
50 mm/min; ISO 527
2.8 %
2.8 %
ASTM D638
Elongation at Yield 2.7 %
2.7 %
Type I, 5 mm/min; ASTM D638
2.7 %
2.7 %
50 mm/min; ISO 527
Tensile Modulus 8.46 GPa
1230 ksi
1 mm/min; ISO 527
8.75 GPa
1270 ksi
50 mm/min; ASTM D638
Flexural Strength 176 MPa
25500 psi
ASTM D790
182 MPa
26400 psi
ISO 178
Flexural Yield Strength 177 MPa
25700 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 6.84 GPa
992 ksi
ASTM D790
7.50 GPa
1090 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.870 J/cm
1.63 ft-lb/in
ASTM D256
Izod Impact, Unnotched 8.17 J/cm
15.3 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 46.0 kJ/m²
21.9 ft-lb/in²
80*10*3; ISO 180/1U
Dart Drop, Total Energy 9.00 J

@Temperature 23.0 °C
6.64 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.47
0.47
ASTM D3702 Modified
Coefficient of Friction, Static 0.46
0.46
ASTM D3702 Modified
K (wear) Factor 70.5 x 10-8 mm³/N-M
35.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 223 °C
433 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
223 °C

@Thickness 3.20 mm
433 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 209 °C
408 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
213 °C

@Thickness 3.20 mm
415 °F

@Thickness 0.126 in
unannealed; ASTM D648