SABIC Innovative Plastics LNP LUBRICOMP ZP001XXP PPE+PS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRICOMP ZP001XXP PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* LUBRICOMP* ZP001XXP is a compound based on PPE+PS resin containing 5% PTFE/Silicone. Added features of this material include: Wear Resistant.
Physical Properties Metric English Comments
Specific Gravity 1.07 g/cc
1.07 g/cc
ASTM D792
Density 1.06 g/cc
0.0383 lb/in³
ASTM D792
Moisture Absorption 0.110 %
0.110 %
50% RH, 24 hrs; ASTM D570
0.150 %
0.150 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm

@Time 86400 sec
0.0080 - 0.010 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.0 MPa
6960 psi
5 mm/min; ISO 527
49.0 MPa
7110 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 45.0 MPa
6530 psi
5 mm/min; ISO 527
49.0 MPa
7110 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 30 %
30 %
Type I, 5 mm/min; ASTM D638
31 %
31 %
5 mm/min; ISO 527
Elongation at Yield 3.2 %
3.2 %
5 mm/min; ISO 527
3.3 %
3.3 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.20 GPa
319 ksi
1 mm/min; ISO 527
2.39 GPa
347 ksi
50 mm/min; ASTM D638
Flexural Strength 73.0 MPa
10600 psi
ISO 178
Flexural Modulus 2.29 GPa
332 ksi
2 mm/min; ISO 178
2.43 GPa
352 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 1.41 J/cm
2.64 ft-lb/in
ASTM D256
Izod Impact, Unnotched 10.4 J/cm
19.5 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 59.0 kJ/m²
28.1 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 18.0 J

@Temperature 23.0 °C
13.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 6.00 J
4.43 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.30
0.30
ASTM D3702 Modified
Coefficient of Friction, Static 0.27
0.27
ASTM D3702 Modified
K (wear) Factor 548 x 10-8 mm³/N-M
272 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 78.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
43.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 78.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
43.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 129 °C
264 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
130 °C

@Thickness 3.20 mm
266 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 116 °C
241 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
118 °C

@Thickness 3.20 mm
244 °F

@Thickness 0.126 in
unannealed; ASTM D648